In this work, we report the synthesis of calcium phosphate–chitosan composite layers. Calcium phosphate layers were deposited on titanium substrates by radio-frequency magnetron sputtering technique by varying the substrate temperature from room temperature (25 °C) up to 100 and 300 °C. Further, chitosan was deposited by matrix-assisted pulsed laser evaporation technique on the calcium phosphate layers. The temperature at the substrate during the deposition process of calcium phosphate layers plays an important role in the embedding of chitosan, as scanning electron microscopy analysis showed. The degree of chitosan incorporation into the calcium phosphate layers significantly influence the physico-chemical properties and the adherence strength of the resulted layers to the substrates. For example, the decreases of Ca/P ratio at the addition of chitosan suggests that a calcium deficient hydroxyapatite structure is formed when the CaP layers are generated on Ti substrates kept at room temperature during the deposition process. The Fourier transform infrared spectroscopy analysis of the samples suggest that the PO₄³⁻/CO₃²⁻ substitution is possible. The X-ray diffraction spectra indicated that the crystalline structure of the calcium phosphate layers obtained at the 300 °C substrate temperature is disturbed by the addition of chitosan. The adherence strength of the composite layers to the titanium substrates is diminished after the chitosan deposition. However, no complete exfoliation of the layers was observed.

The manipulation of magnetic anisotropy represents the fundamental prerequisite for the application of magnetic materials. Here we present the vectorial magnetic properties of nanostructured systems and thin films of Fe and FeCo prepared on linearly trenched Mo templates with thermally controlled periodicity. The magnetic properties of the nanosystems are engineered by tuning the shape, size, thickness, and composition parameters of the thin films. Thus, we control coercivity, magnetization, orientation of the easy axis of magnetization, and the long-range magnetic order of the system in the function of the temperature. We distinguish magnetic components that emerge from the complex morpho-structural features of the undulating Fe or FeCo nanostructured films on trenched Mo templates: (i) assembly of magnetic nanowires and (ii) assembly of magnetic islands/clusters. Uniaxial anisotropy at room temperature was proven, characterized, and explained in the case of all systems. Our work contributes to the understanding of magnetic properties necessary for possible further applications of linear systems and undulated thin films.

The structural properties of VO₂ thin films, grown on either LSAT or Si substrates by pulsed laser deposition (PLD), are elucidated by means of transmission electron microscopy (TEM) methods. The TEM observations confirmed the successful growth of VO₂ by PLD in variable thicknesses, by optimizing the O₂ partial pressure and growth temperature. The films adopt a columnar polycrystalline morphology with narrow columns, up to the film thickness height. Four VO₂ polymorphs have been detected by electron diffraction and high-resolution TEM (HRTEM) analysis, with M1 being by far the most abundant phase. Post-experimental strain measurements in HRTEM images have revealed that the actual residual strain is minimized due to the columnar morphology of the VO₂ grains, as well as intrinsic oxide layers in the VO₂/Si epitaxy. The TEM outcomes confirmed the complementary electrical and magnetic measurements in the films, where a transition from a monoclinic M1 to a rutile VO₂ R phase has been identified, influenced by the initial percentage of phases in thick VO₂ films.

In this work, we report the preparation of nanostructured electrodes based on dense arrays of vertically-aligned copper (Cu) nanowires (NWs) to be subsequently covered by cadmium telluride (CdTe) thin films, with great potential to be used within “substrate”-type photovoltaic cells based on A${}^{\mathrm{I}\mathrm{I}}$-B${}^{\mathrm{V}\mathrm{I}}$ heterojunctions. In particular, the multi-step preparation protocol presented here involves an electrochemical synthesis procedure within a supported anodic aluminum oxide (AAO) nanoporous template for first generating a homogeneous array of vertically-aligned Cu NWs, which are then further embedded within a compact CdTe thin film. In a second stage, we tested three deposition methods (vacuum thermal evaporation, VTE; radio-frequency magnetron sputtering, RF-MS; and electrochemical deposition, ECD) for use in obtaining CdTe layers potentially able to consistently penetrate the previously prepared Cu NWs array. A comparative analysis was performed to critically evaluate the morphological, optical, and structural properties of the deposited CdTe films. The presented results demonstrate that under optimized processing conditions, the ECD approach could potentially allow the cost-effective fabrication of absorber layer/collecting electrode CdTe/Cu nanostructured interfaces that could improve charge collection mechanisms, which in turn could allow the fabrication of more efficient solar cells based on A${}^{\mathrm{I}\mathrm{I}}$-B${}^{\mathrm{V}\mathrm{I}}$ semiconducting compounds.

We report the facile and low-cost preparation as well as detailed characterization of dense arrays of passivated ferromagnetic nickel (Ni) nanotubes (NTs) vertically-supported onto solid Au-coated Si substrates. The proposed fabrication method relies on electrochemical synthesis within the nanopores of a supported anodic aluminum oxide (AAO) template and allows for fine tuning of the NTs ferromagnetic walls just by changing the cathodic reduction potential during the nanostructures’ electrochemical growth. Subsequently, the experimental platform allowed further passivation of the Ni NTs with the formation of ultra-thin antiferromagnetic layers of nickel oxide (NiO). Using adequately adapted magnetic measurements, we afterwards demonstrated that the thickness of the NT walls and of the thin antiferromagneticNiO layer, strongly influences the magnetic behavior of the dense array of exchange-coupled Ni/NiO NTs. The specific magnetic properties of these hybrid ferromagnetic/antiferromagnetic nanosystems were then correlated with the morpho-structural and geometrical parameters of the NTs, as well as ultimately strengthened by additionally-implemented micromagnetic simulations. The effect of the unidirectional anisotropy strongly amplified by the cylindrical geometry of the ferromagnetic/antiferromagnetic interfaces has been investigated with the magnetic field applied both parallel and perpendicular to the NTs axis.

Au_xFe_1−x nanophase thin films of different compositions and thicknesses were prepared by co-deposition magnetron sputtering. Complex morpho-structural and magnetic investigations of the films were performed by X-ray Diffraction, cross-section Transmission Electron Microscopy, Selected Area Electron Diffraction, Magneto Optical Kerr Effect, Superconducting Quantum Interference Device magnetometry and Conversion Electron Mössbauer Spectroscopy. It was proven that depending on the preparation conditions, different configurations of defect α-Fe magnetic clusters, i.e., randomly distributed or auto-assembled in lamellar or filiform configurations, can be formed in the Au matrix. A close relationship between the Fe clustering process and the type of the crystalline structure of the Au matrix was underlined, with the stabilization of a hexagonal phase at a composition close to 70 at. % of Au and at optimal thickness. Due to different types of inter-cluster magnetic interactions and spin anisotropies, different types of magnetic order from 2D Ising type to 3D Heisenberg type, as well as superparamagnetic behavior of non-interacting Fe clusters of similar average size, were evidenced.