Maintaining the bandgap: The bandgap of the black α-phase of formamidinium-based lead triiodide (FAPbI ₃ ) is near optimal for creating high-efficiency perovskite solar cells. However, this phase is unstable, and the additives normally used to stabilize this phase at ambient temperature—such as methylammonium, caesium, and bromine—widen its bandgap. Min et al. show that doping of the α-FAPbI ₃ phase with methylenediammonium dichloride enabled power conversion efficiencies of 23.7%, which were maintained after 600 hours of operation. Unencapsulated devices had high thermal stability and retained >90% efficiency even after annealing for 20 hours at 150°C in air. Science , this issue p. 749

Tetracyclines (TCs) are the most widely used antibiotics for the prevention and treatment of livestock diseases, but they are toxic to humans and have frequently been detected in water bodies. In this study, the physical and chemical properties of the zirconium-based metal organic framework (MOF) UiO-66 and its NH₂-functionalized congener UiO-66-NH₂ were investigated along with batch TC adsorption tests to determine the effect of functionalization on TC removal. TC removal was highest at pH 3 and decreased with increasing pH. Pseudo-1st and pseudo-2nd-order kinetic models were used to study the adsorption equilibrium times, and Langmuir isotherm model was found to be more suitable than Freundlich model. The maximum uptake for UiO-66 and UIO-66-NH₂ was measured to be 93.6 and 76.5 mg/g, respectively. Unexpectedly, the TC adsorption capacity of UiO-66-NH₂ was observed to be lower than that of UiO-66. Density functional theory calculations revealed that the pore structures are irrelevant to TC adsorption, and that the –NH₂ functional group could weaken the structural robustness of UiO-66-NH₂, causing a reduction in TC adsorption capacity. Accordingly, robust MOFs with zirconium-based metal clusters can be effectively applied for the treatment of antibiotics such as TC in water.