In order to modify the porous interfacial transition zone (ITZ) microstructure of concrete more efficiently, a method of coating aggregate surfaces by using several nanoparticles was evaluated in this study. The compressive strength, chloride penetration of sound, and pre-loading samples were assessed in relation to the type of coating materials used (slag, nano-CaCO₃, and nano-SiO₂) and the designed coating thickness (5, 10, and 15 μm). The ITZ microstructure was quantitatively determined via Backscattered electron (BSE) image analysis. Results showed that the overall performance of concrete is highly dependent on the coating materials and the designed coating thickness. Increasing the coating thickness of slag and nano-SiO₂ could improve the chloride penetration resistance but decrease the compressive strength. Using nano-CaCO₃ to coat the aggregate leads to a significant reduction in the properties of the so-prepared concrete. Though coating inert fine particles around aggregate could disturb the initial particle packing and modify the ITZ, it is not able to improve the overall concrete properties. Coating aggregate could determine the ITZ microstructure, especially within the region that is around 30 μm away from aggregate surface.

This paper studies the influence of hydroxyethyl methyl cellulose (HEMC) on the properties of calcium sulfoaluminate (CSA) cement mortar. In order to explore the applicability of different HEMCs in CSA cement mortars, HEMCs with higher and lower molar substitution (MS)/degree of substitution (DS) and polyacrylamide (PAAm) modification were used. At the same time, two kinds of CSA cements with different contents of ye’elimite were selected. Properties of cement mortar in fresh and hardened states were investigated, including the fluidity, consistency and water-retention rate of fresh mortar and the compressive strength, flexural strength, tensile bond strength and dry shrinkage rate of hardened mortar. The porosity and pore size distribution were also analyzed by mercury intrusion porosimetry (MIP). Results show that HEMCs improve the fresh state properties and tensile bond strength of both types of CSA cement mortars. However, the compressive strength of CSA cement mortars is greatly decreased by the addition of HEMCs, and the flexural strength is decreased slightly. The MIP measurement shows that HEMCs increase the amount of micron-level pores and the porosity. The HEMCs with different MS/DS have different effects on the improvement of tensile bond strength in different CSA cement mortars. PAAm modification can improve the tensile bond strength of HEMC-modified CSA cement mortar.

Mineral additions can eliminate the conversion in calcium aluminate hydrates and thus inhibit the future strength retraction of calcium aluminate cement (CAC). However, the impacts of these additions on the protection capacity of CAC concrete in relation to the corrosion of embedded steel reinforcement remains unclear. This paper focused on the corrosion behavior of steel reinforcement in slag, limestone powder, or calcium nitrate-modified CAC mortars via XRD and electrochemical methods (corrosion potential, electrochemical impedance, and linear polarization evaluation). The results indicate that strätlingite (C₂ASH₈), which is formed in slag-modified CAC, has poor chloride-binding ability, leading to decline in corrosion resistance of the steel reinforcement. The electrochemical parameters of specimens immersed in NaCl solution suddenly drop at 14 days, which is 28 days earlier than that of the references. In contrast, the Ca₂[Al(OH)₆]₂0.5CO₃OH·H₂O (CaAl·CO₃²⁻-LDH) and 3CaO·Al₂O₃·Ca(NO₃)₂·12H₂O (NO₃-AFm) in limestone powder and calcium nitrate-modified CAC mortar show great chloride-binding ability, thereby improving the corrosion resistance of the steel reinforcement. The electrochemical parameters of specimens modified with calcium nitrate maintain a slow decreasing trend within 90 days.