The structural, chemical, and electrical properties of amorphous indium gallium zinc oxide (a-IGZO) films by magnetron sputtering and atomic layer deposition (ALD) were investigated where both a-IGZO films had a comparable cation composition. The ALD-derived a-IGZO film exhibited the higher atomic packing density, the effective suppression of trap-like oxygen vacancy defect (Vₒ), and the enhancement in the hybridization of the sp orbital of In, Ga, and Zn cations compared to those of the sputtered a-IGZO film. Hence, a significant improvement in terms of the field-effect mobility was observed for the thin-film transistors with an In0.50Ga0.34Zn0.16O channel by ALD (36.6 cm²/V· s) compared to that of the sputtered In0.48Ga0.38Zn0.14O transistor (20.1 cm²/V· s); the Ion/off ratios for both were ~ 10⁷. Simultaneously, the gate bias stress stability and photobias stress stability were also improved for the IGZO transistors with an ALD-derived channel, which can be explained by its reduced trap-like Vₒ density.

High-mobility indium gallium zinc oxide (IGZO) thin-film transistors (TFTs) are achieved through low-temperature crystallization enabled via a reaction with a transition metal catalytic layer. For conventional amorphous IGZO TFTs, the active layer crystallizes at thermal annealing temperatures of 600 °C or higher, which is not suitable for displays using a glass substrate. The crystallization temperature is reduced when in contact with a Ta layer, where partial crystallization at the IGZO back-channel occurs with annealing at 300 °C, while complete crystallization of the active layer occurs at 400 °C. The field-effect mobility is significantly boosted to 54.0 cm²/V·s for the IGZO device with a metal-induced polycrystalline channel formed at 300 °C compared to 18.1 cm²/V·s for an amorphous IGZO TFT without a catalytic layer. This work proposes a facile and effective route to enhance device performance by crystallizing the IGZO layer with standard annealing temperatures, without the introduction of expensive laser irradiation processes.

Achieving high-performance p-type semiconductors has been considered one of the most challenging tasks for three-dimensional vertically integrated nanoelectronics. Although many candidates have been presented to date, the facile and scalable realization of high-mobility p-channel field-effect transistors (FETs) is still elusive. Here, we report a high-performance p-channel tellurium (Te) FET fabricated through physical vapor deposition at room temperature. A growth route involving Te deposition by sputtering, oxidation and subsequent reduction to an elemental Te film through alumina encapsulation allows the resulting p-channel FET to exhibit a high field-effect mobility of 30.9 cm² V⁻¹ s⁻¹ and an I_ON/OFF ratio of 5.8 × 10⁵ with 4-inch wafer-scale integrity on a SiO₂/Si substrate. Complementary metal-oxide semiconductor (CMOS) inverters using In-Ga-Zn-O and 4-nm-thick Te channels show a remarkably high gain of ~75.2 and great noise margins at small supply voltage of 3 V. We believe that this low-cost and high-performance Te layer can pave the way for future CMOS technology enabling monolithic three-dimensional integration.