Packaging materials based on biodegradable polymers are a viable alternative to replace conventional plastic packaging from fossil origin. The type of plasticizer used in these materials affects their functionality and performance. The effect of different plasticizers such as glycerol (GLY), sorbitol (SOR), and poly(ethylene glycol) (PEG) in concentrations of 5%, 10%, and 15% (w/w) on the structural features and functional properties of starch/PVOH/chitosan films was evaluated. The incorporation of a plasticizer increased the thickness of the biodegradable composite films. Furthermore, the material plasticized with 30% (w/w) sorbitol had the highest elongation at break, lowest water vapor permeability, and better thermal resistance. The results obtained in this study suggest that maize starch/PVOH/chitosan biodegradable composite films are a promising packaging material, and that sorbitol is the most suitable plasticizer for this formulation.

The preparation and characterization of biodegradable films based on starch-PVA-nanoclay by solvent casting are reported in this study. The films were prepared with a relation of 3:2 of starch:PVA and nanoclay (0.5, 1.0, and 1.5% w/v), and glycerol as plasticizer. The nanoclays before being incorporated in the filmogenic solution of starch-PVA were dispersed in two ways: by magnetic stirring and by sonication. The SEM results suggest that the sonication of nanoclay is necessary to reach a good dispersion along the polymeric matrix. FTIR results of films with 1.0 and 1.5% w/v of sonicated nanoclay suggest a strong interaction of hydrogen bond with the polymeric matrix of starch-PVA. However, the properties of WVP, tensile strength, percentage of elongation at break, and Young’s modulus improved to the film with sonicated nanoclay at 0.5% w/v, while in films with 1.0 and 1.5% w/w these properties were even worse than in film without nanoclay. Nanoclay concentrations higher than 1.0 w/v saturate the polymer matrix, affecting the physicochemical properties. Accordingly, the successful incorporation of nanoclays at 0.5% w/v into the matrix starch-PVA suggests that this film is a good candidate for use as biodegradable packaging.

In this work, the miscibility of blends of thermoplastic Achira Starch (AS) and polylactic acid (PLA) was evaluated, assisted by Pluronic® F127 an amphiphilic triblock copolymer that acts as a surfactant and promotes the reduction of surface tension among AS and PLA in solution by emulsion stabilization. Different formulations of AS/PLA blends were obtained at 75:25, 50:50, and 25:75 containing 0 %, 4 %, and 8 % of Pluronic® F127, and glycerol was used as a plasticizer. Solvent casting was the method used to obtain blended polymeric films, which were characterized by Scanning Electron Microscope (SEM), Fourier Transform Infrared Spectroscopy (FTIR), X-ray diffraction (XRD), Thermogravimetric Analysis (TGA), differential scanning calorimetry (DSC) and wettability by contact angle measurements. The results demonstrate that miscibility of PLA in AS or vice versa was achieved. The stability of emulsion and posterior drying of the different formulations allows the production of films for packaging, pharmaceutical, or biomedical applications.