This article deals with electrical discharge machining (EDM) of an alnico alloy, focusing on how key process parameters affect the surface finish. The experiments were conducted using a BP93L EDM machine. The Box–Behnken design was employed to study the effects of three factors, i.e., spark current, pulse-on time, and pulse-off time, each at three levels, on the surface quality. A specially designed system was employed to increase the effectiveness of the machining process by imparting an additional rotary motion to the tool and an additional rotary motion to the workpiece. The aim was to efficiently remove the eroded metal particles and create a surface with smaller craters. The workpiece surface roughness was measured with a Talysurf CCI lite non-contact profiler. During this precision machining process, the arithmetical mean height (Sa) was less than 1 µm. The surface quality was examined also using scanning electron microscopy (SEM) and optical microscopy (OM). The experimental data were analyzed by means of Statistica to determine and graphically represent the relationships between the input and output parameters.

The article presents an example of finishing treatment for aluminum alloys with the use of vibration machining, with loose abrasive media in a closed tumbler. For the analysis of selected properties of the surface layer prepared flat samples of aluminum alloy PA6/2017 in the state after recrystallization. The samples in the first stage were subjected to a treatment of deburring using ceramic media. In a second step polishing process performed with a strengthening metal media. In addition, for comparative purposes was considered. only the case of metal polishing. The prepared samples were subjected to hardness tests and a tangential tensile test. As a result of finishing with vibratory machining, it was possible to remove burrs, flash, rounding sharp edges, smoothing and lightening the surface of objects made. The basic parameters of the surface geometry were obtained using the Talysurf CCI Lite - Taylor Hobson optical profiler. As a result of the tests it can be stated that the greatest reduction of surface roughness and mass loss occurs in the first minutes of the process. Mechanical tests have shown that the most advantageous high values of tensile strength and hardness are obtained with two-stage vibration treatment, - combination of deburring and polishing. Moreover the use of metal media resulted in the strengthening of the surface by pressure deburring with metal media.

This article considers effects of local heat transfer taking place insteel cutting by abrasive water jet machining (AWJM). The influence of temperature changes during AWJM has not been investigated thoroughly. Most studies on AWJM suggest that thermal energy has little or no effect on the material cut. This study focused on the analysis of the material microstructure and indentation microhardness in the jet impact zone and the adjacent area. The structure features revealed through optical metallography and scanning microscopy suggest local temperature changes caused by the impact of the abrasive water jet against the workpiece surface. From the microscopic examinationand hardness tests, it is clear that, during the process, large amounts of energy were transferred locally. The mechanical stress produced by the water jet led to plastic deformation at and near the surface. This was accompanied by the generation and transfer of large amounts of heat resulting in a local rise in temperature to 450 °C or higher.

Measurements enabling the online monitoring of the abrasive waterjet (AWJ) cutting process are still under development. This paper presents an experimental method which can be applicable for the evaluation of the AWJ cutting quality through the measurement of forces during the cutting process. The force measuring device developed and patented by our team has been used for measurement on several metal materials. The results show the dependence of the cutting to deformation force ratio on the relative traverse speed. Thus, the force data may help with a better understanding the interaction between the abrasive jet and the material, simultaneously impacting the improvement of both the theoretical and empirical models. The advanced models could substantially improve the selection of suitable parameters for AWJ cutting, milling or turning with the desired quality of product at the end of the process. Nevertheless, it is also presented that force measurements may detect some undesired effects, e.g., not fully penetrated material and/or some product distortions. In the case of a proper designing of the measuring device, the force measurement can be applied in the online monitoring of the cutting process and its continuous control.

This study was undertaken to look for confirmation that heat transfer induced by abrasive water jet machining (AWJM) affects the microstructure of the material cut. The structure of S235JR carbon steel used in the experiments was reported to change locally in the jet impact zone due to the high concentration of energy generated during cutting with the abrasive water jet. It is assumed that some of the energy is transferred into the material in the form of heat. This is particularly true for materials of considerable thickness with a high thermal conductivity coefficient when cutting is performed at low speeds or with high abrasive consumption. The literature on the subject suggests that in AWJM there is little or no thermal energy effect on the microstructure of the material cut. The research described here involved the measurement of the cutting temperature with thermocouples placed at four different distances from the edge. The distances were measured using computed tomography inspection. The thermocouples used in the tests were capable of detecting temperatures of up to 100 °C. Locally, temperatures at the edge may reach much higher values. The results of the X-ray diffraction qualitative phase analysis reveal that locally the temperatures may be much higher than the eutectoid temperature. Phase changes occurred along the edge since austenite was observed. This suggests that the temperature in the jet impact zone was much higher than the eutectoid temperature. Optical microscopy was also employed to study the material microstructure. Finally, the material nanohardness was determined.

The article aims to characterize Hadfield steel by analyzing its chemical composition, mechanical properties, and microstructure. The study focused on the twinning-induced work hardening of the alloy, which led to an increase in its hardness. The experimental data show that the material hardness at the surface improved considerably after solution heat treatment and work hardening, reaching more than 750 HV. By contrast, the hardness of the material core in the supersaturated condition was about 225 HV. The chemical and phase compositions of the material at the surface were compared with those of the core. The microstructural analysis of the steel revealed characteristic decarburization of the surface layer after solution heat treatment. The article also describes the effects of heat treatment on the properties and microstructure of Hadfield steel. The volumetric (qualitative) analysis of the computed tomography (CT) data of Hadfield steel subjected to heavy dynamic loading helped detect internal flaws, assess the material quality, and potentially prevent the structural failure or damage of the element tested.