Silver nanowires >60 μm have been synthesized using a polyol process without stirring at 130 °C.

The next-generation application of pressure sensors is gradually being extended to include electronic artificial skin (e-skin), wearable devices, humanoid robotics and smart prosthetics. In these advanced applications, high sensing capability is an essential feature for high performance. Although surface patterning treatments and some special elastomeric interlayers have been applied to improve sensitivity, the process is complex and this inevitably raises the cost and is an obstacle to large-scale production. In the present study a simple printing process without complex patterning has been used for constructing the sensor, and an interlayer is employed comprising elastomeric composites filled with silver nanowires. By increasing the relative permittivity, ε_r, of the composite interlayer induced by compression at high nanowire concentration, it has been possible to achieve a maximum sensitivity of 5.54 kPa⁻¹. The improvement in sensitivity did not sacrifice or undermine the other features of the sensor. Thanks to the silver nanowire electrodes, the sensor is flexible and stable after 200 cycles at a bending radius of 2 mm, and exhibits outstanding reproducibility without hysteresis under similar pressure pulses. The sensor has been readily integrated onto an adhesive bandage and has been successful in detecting human movements. In addition to measuring pressure in direct contact, non-contact pressures such as air flow can also be detected.

We demonstrate the fabrication of highly transparent conductive networks on a cellulose nanofiber paper, called cellulose nanopaper. Uniform coating of the conductive nanomaterials, such as silver nanowires (AgNWs) and carbon nanotubes, is achieved by simple filtration of their aqueous dispersions through the cellulose nanopaper, which acts as both filter and transparent flexible substrate. The as-prepared AgNW networks on the nanopaper offer sheet resistance of 12 Ω sq.⁻¹ with optical transparency of 88%, which is up to 75 times lower than the sheet resistance on a polyethylene terephthalate film prepared by conventional coating processes. These results indicate that the ‘filtration coating’ provides uniformly connected conductive networks because of drainage in the perpendicular direction through paper-specific nanopores, whereas conventional coating processes inevitably cause self-aggregation and uneven distribution of the conductive nanomaterials because of the hard-to-control drying process, as indicated by the well-known coffee-ring effect. Furthermore, the conductive networks are embedded in the surface layer of the nanopaper, showing strong adhesion to the nanopaper substrate and providing foldability with negligible changes in electrical conductivity. This filtration process is thus expected to offer an effective coating approach for various conductive materials, and the resulting transparent conductive nanopaper is a promising material for future paper electronics.

Topochemical synthesis of gold nanoparticles (AuNPs) was achieved on crystalline cellulose single nanofibers (CSNFs), which were tailored from native cellulose. Exposed AuNPs@CSNFs composite exhibited an excellent catalytic efficiency: the turnover frequency of the AuNPs@CSNFs was up to 840 times that of conventional polymer-supported AuNPs, for a model aqueous reduction reaction. Our novel strategy provides a promising solution to realize efficient use of limited noble metals using natural bioresources.