Among different organic fillers, the chemical composition of Syzygium aromaticum, commonly known as cloves, has great potential as a sustainable reinforcement for polymeric materials. In the study, grounded cloves were used as cellulosic filler for a novel polyurethane (PU) composite foams. Soybean oil-based PU composite foams were successfully reinforced with different concentrations (1, 2, and 5 wt%) of clove filler. PU foams were examined by rheological behavior, processing parameters, cellular structure (scanning electron microscopy analysis), mechanical properties (compression test, impact test, three-point bending test), thermal properties (thermogravimetric analysis), viscoelastic behavior (dynamic mechanical analysis) as well as selected application properties (apparent density, dimensional stability, surface hydrophobicity, water absorption, color characteristic). In order to undertake the disc diffusion method, all PU composites were tested against selected bacteria (Escherichia coli and Staphylococcus aureus). Based on the results, it can be concluded that the addition of 1 and 2 wt% of clove filler leads to PU composite foams with improved compression strength (improvement by ≈18% for sample PU-1), greater flexural strength (increase of ≈11%), and improved impact strength (increase of ≈8%). Moreover, it has been proved that clove filler may be used as a natural anti-aging compound for polymeric materials. Based on the antibacterial results, it has been shown that the addition of clove filler significantly improved the antibacterial properties of PU foams and is suitable for the manufacturing of antimicrobial PU composite foams. Due to these positive and beneficial effects, it can be stated that the use of cloves as a natural filler in PU composite foams can promote a new application path in converting agricultural waste into useful resources for creating a new class of green materials.

In this work, rigid polyurethane (PUR) foams were prepared by incorporating 2 wt% of eucalyptus fibers. The eucalyptus fibers were surface-modified by maleic anhydride, alkali, and silane (triphenylsilanol) treatment. The impact of the modified eucalyptus fibers on the mechanical, thermal, and fire performances of polyurethane foams was analyzed. It was observed that the addition of eucalyptus fibers showed improved mechanical and thermal properties and the best properties were shown by silane-treated fibers with a compressive strength of 312 kPa and a flexural strength of 432 kPa. Moreover, the thermal stability values showed the lowest decline for polyurethane foams modified with the silane-treated fibers, due to the better thermal stability of such modified fibers. Furthermore, the flame resistance of polyurethane foams modified with the silane-treated fibers was also the best among the studied composites. A cone calorimetry test showed a decrease in the peak of heat release from 245 to 110 kW∙m⁻² by the incorporation of silane-treated fibers. Furthermore, total heat release and total smoke release were also found to decrease remarkably upon the incorporation of silane-treated fibers. The value of limiting oxygen index was increased from 20.2% to 22.1%. Char residue was also found to be increased from 24.4% to 28.3%. It can be concluded that the application of chemically modified eucalyptus fibers has great potential as an additive to incorporate good mechanical, thermal, and fire properties in rigid polyurethane foams.