One of the solutions for overheating the interior in the summer without increasing energy consumption is the integration of phase change material (PCM) into interior plasters. However, adding PCM to plasters deteriorates their properties and thus their usability. The aim of this paper is to determine how the microencapsulated PCM affects the mechanical, thermal, and fire properties of plasters and how much PCM can be added to the plaster. Two sets of samples were prepared: in set S, part of the aggregate was replaced by PCM; and in set R, only PCM was added. The bulk density, flexural strength, compressive strength, tensile strength perpendicular to the surface, thermal conductivity coefficient, specific heat capacity, melting, and solidification temperatures and enthalpy were measured. A single-flame source fire test and a gross heat of combustion fire test were performed to determine the reaction to the fire class. The results show that with an increasing proportion of PCM, the strength of the samples of set R decreased more significantly than it did with the samples of set S. It was found that only up to about 10% PCM could be added to set R, while up to 30% PCM could be added to set S.

Straw bales can be used as a relatively cheap and ecological building material for buildings. Design of straw buildings is currently based on empirical knowledge although it would be very helpful to have more information about material properties for designing and realization of straw bales houses. Article discuses load - deformation behavior of straw bales in laboratory conditions and evaluate the modulus of elasticity of local straw bales. Deformation characteristics of straw bales can be very useful for the design of straw buildings.

Sustainable development in civil engineering is the clear and necessary goal of the current generation. There are many possibilities for reducing the use of depletable resources. One of them is to use renewable and recyclable materials on a larger scale in the construction industry. One possibility is the application of natural thermal insulators. A typical example is a crushed straw, which is generated as agricultural waste in the Czech Republic. Due to its small dimensions and good thermal insulation parameters, this material can also be used as blown thermal insulation. The research aims to examine the fire resistance of crushed straw as blown insulation. The single-flame source fire test results, thermal attack by a single burning item (SBI) test and large-scale test of a perimeter wall segment are shown. The results show that blown insulation made of crushed straw meets the requirements of fire protection. In addition, crushed straw can be also used to protect load-bearing structures due to its behaviour. This article also shows the production process of crushed straw used as blown insulation in brief.

Paper presents results of measuring of airtightness and acoustic properties of clay house. This clay house was built as a "SuperAdobe house" from the bags filled with clay. Construction of the clay house is a cupola. Objective of the measurement was to evaluate the quality of peripheral construction in terms of airtightness. We also wanted to verify the acoustic parameters of earthen structures and determine the value of airborne sound insulation.

The importance of green and sustainable materials in civil engineering is undeniable. Alongside modern practices that improve the properties of standard building materials, there are ways to revive forgotten techniques, including straw bale buildings. Straw bales are load-bearing structures, which are applied based on handed-down experience and lack standard approaches in testing, design, and application. Therefore, a goal ahead is to describe every aspect of the process in technical detail. The objective of this paper is to highlight practical ideas for testing straw bales on a hydraulic press machine and to provide a basic statistical investigation of the results obtained. Two basic series were prepared, one without a side barrier and the other with a side barrier. The reason for this was to delineate the limits of the real behaviour of the straw bale on the load bearing wall of the house. Due to the assumed slight embedment of adjacent bales, the real result were within these limits. The experimental plan, basic results, simplified correlations, and statistical evaluation are presented. Recommendations for a further testing and evaluation are provided. As expected, the results with and without the lateral barrier differ by almost 18% for the true strain.

This paper describes the results of a scientific project focused on determining of the Airborne Sound Insulation of a peripheral non-load bearing wall made of straw bales expressed by Weighted Sound Reduction Index. Weighted Sound Reduction Index was determined by measuring in the certified acoustic laboratory at the Faculty of Mechanical Engineering at Brno University of Technology. The measured structure of the straw wall was modified in combinations with various materials, so the results include a wide range of possible compositions of the wall. The key modification was application of plaster on both sides of the straw bale wall. This construction as is frequently done in actual straw houses. The additional measurements were performed on the straw wall with several variants of additional wall of slab materials. The airborne sound insulation value has been also measured in separate stages of the construction. Thus it is possible to compare and determinate the effect of the single layers on the airborne sound insulation.