Directed energy deposition (DED) is a family of additive manufacturing technologies. With these processes, metal parts are built layer by layer, introducing dynamics that propagate in time and layer-domains, which implies additional complexity and consequently, the resulting part quality is hard to predict. Control of the deposit layer thickness and height is a critical issue since it impacts on geometrical accuracy, process stability, and the overall quality of the product. Therefore, online feedback height control for DED processes with proper sensor strategies is required. This work presents a novel vision-based triangulation technique through an off-axis located CCD camera synchronized with a 640 nm wavelength pulsed illumination laser. Image processing and machine vision techniques allow in-line height measurement right after metal solidification. The linearity and the precision of the proposed setup are validated through off-and in-process trials in the laser metal deposition (LMD) process. Besides, the performance of the developed in-line inspection system has also been tested for the Arc based DED process and compared against experimental weld bead characterization data. In this last case, the system additionally allowed for the measurement of weld bead width and contact angles, which are critical in first runs of multilayer buildups.

In this work, the manufacture of thin walls with sharp corners has been optimized by adjusting the limits of a 3-axis cartesian kinematics through data recorded and analyzed off-line, such as axis speed, acceleration and the positioning of the X and Y axes. The study was carried out with two powder materials (SS316L and IN718) using the directed energy deposition process with laser. Thin walls were obtained with 1 mm thickness and only one bead per layer and straight/sharp corners at 90°. After adjusting the in-position parameter G502 for positioning precision on the FAGOR 8070 CNC system, it has been possible to obtain walls with minimal accumulation of material in the corner, and with practically constant layer thickness and height, with a radii of internal curvature between 0.11 and 0.24 mm for two different precision configuration. The best results have been obtained by identifying the correct balance between the decrease in programmed speed and the precision in the positioning to reach the point defined as wall corner, with speed reductions of 29% for a programmed speed of 20 mm/s and 61% for a speed of 40 mm/s. The walls show minimal defects such as residual porosities, and the microstructure is adequate.

In this work, the manufacture of thin walls with sharp corners has been optimized by adjusting the limits of a 3-axis cartesian kinematics through data recorded and analyzed off-line, such as axis speed, acceleration and the positioning of the X and Y axes. The study was carried out with two powder materials (SS316L and IN718) using the directed energy deposition process with laser. 1 mm thick walls were obtained with only one bead per layer and straight/sharp corners at 90º. After adjusting the in-position parameter G502 for positioning precision on the FAGOR 8070 CNC system, it has been possible to obtain walls with minimal accumulation of material in the corner, and with practically constant layer thickness and height, with a radii of internal curvature between 0.11 and 0.24 mm for two different precision configuration. The best results have been obtained by identifying the correct balance between the decrease in programmed speed and the precision in the positioning to reach the point defined as wall corner, with speed reductions of 29% for a programmed speed of 20 mm/s and 61% for a speed of 40 mm/s. The walls show minimal defects such as residual porosities, and the microstructure is adequate.