Integrating nano- to micro-sized dielectric fillers to elastomer matrices to form dielectric composites is one of the commonly utilized methods to improve the performance of dielectric elastomer actuators (DEAs). Barium titanate (BaTiO₃) is among the widely used ferroelectric fillers for this purpose; however, calcium copper titanate CaCu₃Ti₄O₁₂ (CCTO) has the potential to outperform such conventional fillers. Despite their promising performance, CCTO-based dielectric composites for DEA application are studied to a relatively lower degree. Particularly, the composites are characterized for a comparably small particle loading range, while critical DEA properties such as breakdown strength and nonlinear elasticity are barely addressed in the literature. Thus, in this study, CCTO was paired with polydimethylsiloxane (CH₃)₃SiO[Si(CH₃)₂O]_nSi(CH₃)₃ (PDMS), Sylgard 184, to gain a comprehensive understanding of the effects of particle loading and size on the dielectric composite properties important for DEA applications. The dielectric composites’ performance was described through the figures of merit (FOMs) that consider materials’ Young’s modulus, dielectric permittivity, and breakdown strength. The optimum amounts of the ferroelectric filler were determined through the FOMs to maximize composite DEA performance. Lastly, electromechanical testing of the pre-stretched CCTO-composite DEA validated the improved performance over the plain elastomer DEA, with deviations from prediction attributed to the studied composites’ nonlinearity.

Recent developments in micro-scale additive manufacturing (AM) have opened new possibilities in state-of-the-art areas, including microelectromechanical systems (MEMS) with intrinsically soft and compliant components. While fabrication with soft materials further complicates micro-scale AM, a soft photocurable polydimethylsiloxane (PDMS) resin, IP-PDMS, has recently entered the market of two-photon polymerization (2PP) AM. To facilitate the development of microdevices with soft components through the application of 2PP technique and IP-PDMS material, this research paper presents a comprehensive material characterization of IP-PDMS. The significance of this study lies in the scarcity of existing research on this material and the thorough investigation of its properties, many of which are reported here for the first time. Particularly, for uncured IP-PDMS resin, this work evaluates a surface tension of 26.7 ± 4.2 mN/m, a contact angle with glass of 11.5 ± 0.6°, spin-coating behavior, a transmittance of more than 90% above 440 nm wavelength, and FTIR with all the properties reported for the first time. For cured IP-PDMS, novel characterizations include a small mechanical creep, a velocity-dependent friction coefficient with glass, a typical dielectric permittivity value of 2.63 ± 0.02, a high dielectric/breakdown strength for 3D-printed elastomers of up to 73.3 ± 13.3 V/µm and typical values for a spin coated elastomer of 85.7 ± 12.4 V/µm, while the measured contact angle with water of 103.7 ± 0.5°, Young’s modulus of 5.96 ± 0.2 MPa, and viscoelastic DMA mechanical characterization are compared with the previously reported values. Friction, permittivity, contact angle with water, and some of the breakdown strength measurements were performed with spin-coated cured IP-PDMS samples. Based on the performed characterization, IP-PDMS shows itself to be a promising material for micro-scale soft MEMS, including microfluidics, storage devices, and micro-scale smart material technologies.

Magnetorheological (MR) fluid is a smart material utilized for semi-active damping devices thanks to its ability to become viscoelastic solid under a magnetic field and provide variable damping. While most of these devices primarily utilize the fluid’s drastic increase in viscosity, its variable stiffness is rarely utilized. A MR fluid filled spring is a novel device with variable stiffness and damping and is the subject of the present study. First, the derived analytical model and the device’s controllable stiffness capability were experimentally validated by performing tensile tests with a fabricated hollow polymer spring filled with MRF-132DG. The analytical model was proved to describe the MR fluid static effect of increased spring stiffness accurately. Secondly, dynamic testing demonstrated the device’s controllable damping and capability to shift natural frequencies. In addition, the testing unveiled an enhanced dynamic performance of the spring due to the cumulative effect of MR fluid activation and specifically aligned uniform magnetic field. Finally, the hollow spring design was optimized through analytical and non-linear finite element buckling analysis to maximize MR fluid stiffness effect. The resulting critical parameters of the optimized design were used to estimate the effects of hollow spring material and operating conditions on the variable stiffness of the device.