A novel polymer bio-composite based on nano-hydroxyapatite (n-Hap) and chitosan (CS) (CS/n-Hap) was synthesized to effectively address toxic cadmium ions removal from water. The composition and structure of CS/n-Hap bio-composite were analyzed through different characterization techniques. XRD patterns affirmed that the crystalline structure of n-Hap remained unaltered during CS/n-Hap synthesis, while FT-IR spectrum sustained all the characteristic peaks of both CS and n-Hap, affirming the successful synthesis of CS/n-Hap. Adsorption studies, including pH, adsorbent dosage, contact time, initial Cd(II) concentration, and temperature, were carried out to explain and understand the adsorption mechanism. Comparatively, CS/n-Hap bio-composite exhibited better Cd(II) adsorption capacity than pristine CS, with an experimental maximum uptake of 126.65 mg/g under optimized conditions. In addition, the kinetic data were well fitted to the pseudo-second-order model, indicating the formation of chemical bonds between Cd(II) and CS/n-Hap during adsorption. Furthermore, the thermodynamic study suggested that Cd(II) adsorption onto CS/n-Hap was endothermic and spontaneous. The regeneration study showed only about a 3% loss in Cd(II) uptake by CS/n-Hap after five consecutive cycles. Thus, a simple and facile approach was here developed to synthesize an eco-friendly and cost-effective material that can be successfully employed for the removal of toxic heavy metal ions from water.

In this work, chitosan, a biopolymer was cross-linked using glutaraldehyde (Gl) and modified by natural apatite. The Cs-Gl@Fap composite was used to adsorb methyl orange from an aqueous solution. The materials were characterised by SEM-EDX, FTIR, XRD and TGA-DTG analysis confirming the successful synthesis of Cs-Gl@Fap. The effects of experimental variables on adsorption efficiency were examined. Adsorption studies showed that the maximum adsorption capacity was 225.55 mg/g at an equilibration time of 120 min. The pseudo-second-order rate expression supported data best, while the Langmuir equation could satisfactorily describe isotherm data. The thermodynamic constants of the adsorption process were evaluated. The results showed that the stabilisation by contact of methyl orange on Cs-Gl@Fap was endothermic and spontaneous. Additionally, when reused, the hybrid adsorbent remains at approximately 83% of its original capacity after five adsorption cycles.

Chitosan (Cs)-based composites were developed by incorporating silica (Cs–Si), and both silica and hydroxyapatite (Cs–Si–Hap), comparatively tested to sequester hexavalent (Cr(VI)) ions from water. XRD and FT-IR data affirmed the formation of Cs–Si and Cs–Si–Hap composite. Morphological images exhibits homogeneous Cs–Si surface, decorated with SiO₂ nanoparticles, while the Cs–Si–Hap surface was non-homogeneous with microstructures, having SiO₂ and Hap nanoparticles. Thermal analysis data revealed excellent thermal stability of the developed composites. Significant influence of pH, adsorbent dose, contact time, temperature, and coexisting anions on Cr(VI) adsorption onto composites was observed. Maximum Cr(VI) uptakes on Cs and developed composites were observed at pH 3. The equilibration time for Cr(VI) adsorption on Cs–Si–Hap was 10 min, comparatively better than Cs and Cs–Si. The adsorption data was fitted to pseudo-second-order kinetic and Langmuir isotherm models with respective maximum monolayer adsorption capacities (q_m) of 55.5, 64.4, and 212.8 mg/g for Cs, Cs–Si, and Cs–Si–Hap. Regeneration studies showed that composites could be used for three consecutive cycles without losing their adsorption potential.

In this work, a cost-effective chitin-based magnesium oxide (CHt@MgO) biocomposite with excellent anionic methyl orange (MO) dye removal efficiency from water was developed. The CHt@MgO biocomposite was characterized by FT-IR, XRD, SEM-EDX, and TGA/DTG. Results proved the successful synthesis of CHt@MgO biocomposite. Adsorption of MO on the CHt@MgO biocomposite was optimized by varying experimental conditions such as pH, amount of adsorbent (m), contact time (t), temperature (T), and initial MO concentration (C_o). The optimized parameters for MO removal by CHt@MgO biocomposite were as follows: pH, 6; m, 2 g/L; t, 120 min. Two common isotherm models (Langmuir and Freundlich) and three kinetic models (pseudo-first-order (PFO), pseudo-second-order (PSO), and intraparticle diffusion (IPD)) were tested for experimental data fitting. Results showed that Langmuir and PFO were the most suitable to respectively describe equilibrium and kinetic results on the adsorption of MO adsorption on CHt@MgO biocomposite. The maximum Langmuir monolayer adsorption capacity (q_m) on CHt@MgO biocomposite toward MO dye was 252 mg/g at 60 °C. The reusability tests revealed that CHt@MgO biocomposite possessed high (90.7%) removal efficiency after the fifth regeneration cycle.