Poly(p-phenylene terephthalamide) (PPTA) and ultra-high-molecular-weight polyethylene (UHMWPE) are high-performance polymer materials largely used for body armor applications. Although composite structures from a combination of PPTA and UHMWPE have been created and described in the literature, the manufacture of layered composites from PPTA fabrics and UHMWPE films with UHMWPE film as an adhesive layer has not been reported. Such a new design can provide the obvious advantage of simple manufacturing technology. In this study, for the first time, we prepared PPTA fabrics/UHMWPE films laminate panels using plasma treatment and hot-pressing and examined their ballistic performance. Ballistic testing results indicated that samples with moderate interlayer adhesion between PPTA and UHMWPE layers exhibited enhanced performance. A further increase in interlayer adhesion showed a reverse effect. This finding implies that optimization of interface adhesion is essential to achieve maximum impact energy absorption through the delamination process. In addition, it was found that the stacking sequence of the PPTA and UHMWPE layers affected ballistic performance. Samples with PPTA as the outermost layer performed better than those with UHMWPE as the outermost layer. Furthermore, microscopy of the tested laminate samples showed that PPTA fibers exhibited shear cutting failure on the entrance side and tensile failure on the exit side of the panel. UHMWPE films exhibited brittle failure and thermal damage at high compression strain rate on the entrance side and tensile fracture on the exit side. For the first time, findings from this study reported in-field bullet testing results of PPTA/UHMWPE composite panels, which can provide important insights for designing, fabricating, and failure analysis of such composite structures for body armors.

A novel hybrid of Cu nanoparticles/three-dimensional graphene/Ni foam (Cu NPs/3DGr/NiF) was prepared by chemical vapor deposition, followed by a galvanic displacement reaction in Ni- and Cu-ion-containing salt solution through a one-step reaction. The as-prepared Cu NPs/3DGr/NiF hybrid is uniform, stable, recyclable and exhibits an extraordinarily high catalytic efficiency for the reduction of 4-nitrophenol (4-NP) to 4-aminophenol (4-AP) with a reduction rate constant K = 0.056 15 s ⁻¹ , required time ∼30 s and excellent sensing properties for the non-enzymatic amperometric hydrogen peroxide (H ₂ O ₂ ) with a linear range ∼50 μ M–9.65 mM, response time ∼3 s, detection limit ∼1 μ M. The results indicate that the as-prepared Cu NPs/3DGr/NiF hybrid can be used to replace expensive noble metals in catalysis and sensing applications.

Poly(p-phenylene terephthalamide) (PPTA) is a high-performance polymer that has been utilized in a range of applications. Although PPTA fibers are widely used in various composite materials, laminar structures consisting of PPTA and ultra-high-molecular-weight polyethylene (UHMWPE), are less reported. The difficulty in making such composite structures is in part due to the weakness of the interface formed between these two polymers. In this study, a layered structure was produced from PPTA fabrics and UHMWPE films via hot pressing. To improve the interlayer adhesion, oxygen plasma was used to treat the PPTA and the UHMWPE surfaces prior to lamination. It has been found that while plasma treatment on the UHMWPE surface brought about a moderate increase in interlayer adhesion (up to 14%), significant enhancement was achieved on the samples fabricated with plasma treated PPTA (up to 91%). It has been assumed that both surface roughening and the introduction of functional groups contributed to this improvement.

The application of Au nanoparticles (Au NPs) often requires surface modification with chemical surfactants, which dramatically reduce the surface activity and increase the chemical contamination and cost of Au NPs. In this research, we have developed a novel Au NPs/reduced graphene oxide/Ni foam hybrid (Au NPs/RGO/NiF) by in situ reduction through ascorbic acid and replacement reaction. This method is green, facile and efficient. The Au NPs are free of chemical surfactants and are homogeneously distributed on the surface of the RGO/NiF. The as-prepared Au NPs/RGO/NiF hybrid is uniform, stable and exhibits not only a high reduction efficiency for the reduction of 4-nitrophenol with a catalytic kinetic constant of up to 0.46 min ⁻¹ (0.15 cm ³ catalysis) but also a sensitive and selective detection of H ₂ O ₂ with a detection limit of ∼1.60 μ M.

Cetyltrimethylammonium bromide (CTAB) surfactant was used as both a synthesis and dispersion template for nanoporous silica to create high-performance biogenic straw-based thermal insulation composites.