The present study is focused on the synthesis and structural properties of amorphous terbium metal–organic framework thin film (TbMOF-TF) and its transformation to terbium oxide by pyrolysis at 450 °C in the air. The crystalline (cTbMOF) and amorphous (aTbMOF) films were prepared by solvothermal synthesis using different amounts (0.4 and 0.7 mmol) of the modulator (sodium acetate), respectively. The powders were characterized by differential scanning calorimetry (DSC), thermogravimetry (TG), Fourier transform infrared (FTIR), Raman spectroscopy, and scanning electron microscopy (SEM). The varied chemical composition of the surface of TbMOFs and Tb_xO_y was investigated by X-ray photoelectron spectroscopy (XPS). X-ray diffraction (XRD) and transmission electron microscopy (TEM) revealed that aTbMOF had been fully transformed to a Tb₄O₇ phase with a cubic crystal structure at 450 °C. The amorphous aTbMOF-TF film was prepared by dropping a colloidal solution of amorphous precursor nanocrystals on the SiO₂/Si substrates covered with Pt as an interlayer. XPS confirmed the presence of Tb in two states, Tb³⁺ and Tb⁴⁺. The amorphous film has a rough, porous microstructure and is composed of large clusters of worm-like particles, while terbium oxide film consists of fine crystallites of cubic fluorite cF-TbO_x, c-Tb₄O_7, and c-Tb₂O₃ phases. The surface topography was investigated by a combination of confocal (CM) and atomic force microscopy (AFM). The amorphous film is porous and rough, which is contrast to the crystalline terbium oxide film.

Lanthanide Metal–Organic Frameworks (LnMOFs), in recent years, have developed into an interesting subclass of MOFs. While the number of published papers, in particular, were dedicated to their synthesis and functional properties, along with the application mechanisms of MOFs, only a few of them have been focused on LnMOFs thin films independently. LnMOFs have become interesting thanks to their outstanding properties, for example, excellent structural flexibility, tunable pore size, surface area, functionality, and good chemical stability. Significant progress over the past two decades in the preparation of MOF films has been achieved, especially towards the development of green, or at least greener, synthesis approaches. We begin with insight into various types of MOFs and summarize recent achievements in the production of LnMOF films, along with various film preparation approaches. Afterward, we briefly discuss the applications of luminescence features of lanthanide ions in films and their potential as white-light source materials. We also covered films based on Eu, Tb, and Gd with particular accents on different design approaches. Moreover, specifically, luminescent features applied for sensing temperature, a variety of ions, gases, and biomolecules are highlighted. The review ends with a comprehensive conclusion about the state-of-art-potential of LnMOFs together with an outlook on the future of LnMOF films in future technologies.

This study presents the synthesis, structural and luminescence properties for lanthanide metal–organic frameworks (LnMOFs), which belong to the sub-class of coordination polymers. The series of nanosized LnMOFs (Ln = Eu, Gd, Tb, Eu_0.5Gd_0.5, Tb_0.5Gd_0.5 and Eu_0.5Tb_0.5) was prepared by solvothermal synthesis using a modulator (sodium acetate). We investigated the various surface chemistry compositions of the isostructural LnMOFs with a [Ln(btc)] structure (BTC: Benzene-1,3,5-tricarboxylate) by X-ray photoelectron spectroscopy (XPS). The XPS confirmed the mixed-valent Eu³⁺ and Eu²⁺ compounds, and the presence of Tb in both +3 and +4 valence states, and one +3 valency of Gd. A nanostructure of mixed LnMOFs (EuGd, TbGd and EuTb) with a rod-like shape is related to luminescence properties. The MOFs (EuTb and EuGd) presented Comission Internationale de l’Éclairage (CIE) chromaticities of x = 0.666 and y = 0.331, and x = 0.654 and y = 0.348, respectively, in the red region. They were better than the values desired for use in commercial phosphors, which are x = 0.64 and y = 0.35. For [Tb/Gd(btc)], the CIE coordinates were x = 0.334 and y = 0.562, presenting emissions in the green region. Bimetallic LnMOFs are very promising UV light sensors for biological applications.