The aim of the work was to prepare a polymer matrix composite doped by silver nanoparticles and analyze the influence of silver nanoparticles (AgNPs) on polymers’ optical and toxic properties. Two different colloids of AgNPs were prepared by chemical reduction. The first colloid, a blue one, contains stable triangular nanoparticles (the mean size of the nanoparticles was ~75 nm). UV–vis spectrophotometry showed that the second colloid, a yellow colloid, was very unstable. Originally formed spherical particles (~11 nm in diameter) after 25 days changed into a mix of differently shaped nanoparticles (irregular, triangular, rod-like, spherical, decahedrons, etc.), and the dichroic effect was observed. Pre-prepared AgNPs were added into the PVA (poly(vinyl alcohol)) polymer matrix and PVA–AgNPs composites (poly(vinyl alcohol) doped by Ag nanoparticles) were prepared. PVA–AgNPs thin layers (by a spin-coating technique) and fibers (by electrospinning and dip-coating techniques) were prepared. TEM and SEM techniques were used to analyze the prepared composites. It was found that the addition of AgNPs caused a change in the optical and antibiofilm properties of the non-toxic and colorless polymer. The PVA–AgNPs composites not only showed a change in color but a dichroic effect was also observed on the thin layer, and a good antibiofilm effect was also observed.

The aim of the work was to prepare polymer matrix composite (PMC) microfibers doped by green synthesized silver nanoparticles (AgNPs). The incorporation of AgNP into the polymer matrix can provide toxic properties to the polymer. Polyvinyl alcohol (PVA) was used as a matrix. AgNPs were synthesized by the green method, where the leaf extract of Rosmarinus officinalis (R. officinalis) was used as a reduction and capping agent. PVA-AgNPs composites were prepared in two ways: the ex situ method (pre-prepared globular AgNPs with a mean diameter of 20 nm were added into polymer matrix) and the in situ method (AgNPs were synthesized in the process of polymer composite preparation; in situ synthesized nanoparticles were a mix of different shapes with a mean diameter of ~100 nm). FTIR (Infrared spectroscopy with Fourier Transformation), UV–vis (Ultraviolet–visible spectroscopy), TEM (Transmission Electron Microscope), EDX (Energy-dispersive X-ray spectroscopy), and SEM (Scanning Electron Microscope) techniques were used for the analysis of nanoparticles and prepared PMCs. Thin layers and microfibers of in situ and ex situ PMCs were prepared. The presence of AgNPs clusters was evident in both PMC thin layers. After electrospinning, the chains of nanoparticles were observed inside the fibers. The distribution of nanoparticles was improved by increasing the AgNPs volume fraction (from 5 vol.% to 20 vol.%). Toxic and antibiofilm activity of AgNPs colloid, pure PVA, and PVA-AgNPs composites against the one-cell green algae Parachlorella kessleri (P. kessleri) was analyzed. AgNPs colloid, as well as PVA-AgNPs composites, showed good toxic and antibiofilm activity, and pure PVA shows no toxic/antibiofilm activity.

The present study is focused on the synthesis and structural properties of amorphous terbium metal–organic framework thin film (TbMOF-TF) and its transformation to terbium oxide by pyrolysis at 450 °C in the air. The crystalline (cTbMOF) and amorphous (aTbMOF) films were prepared by solvothermal synthesis using different amounts (0.4 and 0.7 mmol) of the modulator (sodium acetate), respectively. The powders were characterized by differential scanning calorimetry (DSC), thermogravimetry (TG), Fourier transform infrared (FTIR), Raman spectroscopy, and scanning electron microscopy (SEM). The varied chemical composition of the surface of TbMOFs and Tb_xO_y was investigated by X-ray photoelectron spectroscopy (XPS). X-ray diffraction (XRD) and transmission electron microscopy (TEM) revealed that aTbMOF had been fully transformed to a Tb₄O₇ phase with a cubic crystal structure at 450 °C. The amorphous aTbMOF-TF film was prepared by dropping a colloidal solution of amorphous precursor nanocrystals on the SiO₂/Si substrates covered with Pt as an interlayer. XPS confirmed the presence of Tb in two states, Tb³⁺ and Tb⁴⁺. The amorphous film has a rough, porous microstructure and is composed of large clusters of worm-like particles, while terbium oxide film consists of fine crystallites of cubic fluorite cF-TbO_x, c-Tb₄O_7, and c-Tb₂O₃ phases. The surface topography was investigated by a combination of confocal (CM) and atomic force microscopy (AFM). The amorphous film is porous and rough, which is contrast to the crystalline terbium oxide film.

Lanthanide Metal–Organic Frameworks (LnMOFs), in recent years, have developed into an interesting subclass of MOFs. While the number of published papers, in particular, were dedicated to their synthesis and functional properties, along with the application mechanisms of MOFs, only a few of them have been focused on LnMOFs thin films independently. LnMOFs have become interesting thanks to their outstanding properties, for example, excellent structural flexibility, tunable pore size, surface area, functionality, and good chemical stability. Significant progress over the past two decades in the preparation of MOF films has been achieved, especially towards the development of green, or at least greener, synthesis approaches. We begin with insight into various types of MOFs and summarize recent achievements in the production of LnMOF films, along with various film preparation approaches. Afterward, we briefly discuss the applications of luminescence features of lanthanide ions in films and their potential as white-light source materials. We also covered films based on Eu, Tb, and Gd with particular accents on different design approaches. Moreover, specifically, luminescent features applied for sensing temperature, a variety of ions, gases, and biomolecules are highlighted. The review ends with a comprehensive conclusion about the state-of-art-potential of LnMOFs together with an outlook on the future of LnMOF films in future technologies.

This study presents the synthesis, structural and luminescence properties for lanthanide metal–organic frameworks (LnMOFs), which belong to the sub-class of coordination polymers. The series of nanosized LnMOFs (Ln = Eu, Gd, Tb, Eu_0.5Gd_0.5, Tb_0.5Gd_0.5 and Eu_0.5Tb_0.5) was prepared by solvothermal synthesis using a modulator (sodium acetate). We investigated the various surface chemistry compositions of the isostructural LnMOFs with a [Ln(btc)] structure (BTC: Benzene-1,3,5-tricarboxylate) by X-ray photoelectron spectroscopy (XPS). The XPS confirmed the mixed-valent Eu³⁺ and Eu²⁺ compounds, and the presence of Tb in both +3 and +4 valence states, and one +3 valency of Gd. A nanostructure of mixed LnMOFs (EuGd, TbGd and EuTb) with a rod-like shape is related to luminescence properties. The MOFs (EuTb and EuGd) presented Comission Internationale de l’Éclairage (CIE) chromaticities of x = 0.666 and y = 0.331, and x = 0.654 and y = 0.348, respectively, in the red region. They were better than the values desired for use in commercial phosphors, which are x = 0.64 and y = 0.35. For [Tb/Gd(btc)], the CIE coordinates were x = 0.334 and y = 0.562, presenting emissions in the green region. Bimetallic LnMOFs are very promising UV light sensors for biological applications.

During hot-dip galvanization, wastes such as bottom dross, zinc ash, spent pre-treatment solutions, and galvanizing flue dust (GFD) are generated. In scientific publications, research devoted to GFD waste recycling is absent, and companies generating this waste require a solution to this complex problem. GFD is often landfilled in hazardous waste landfills. However, it is possible to process this waste hydrometallurgically, where GFD is first leached, the solution is refined, and finally, zinc metal is obtained by electrowinning. During specific environmentally friendly leaching, not all solid GFD is dissolved, and the aim of this study is to process the remaining solid GFD residue. The analysis shows that the GFD residue material mainly contains zinc (42.46%) in the form of oxides, but there is also a small amount of polluting elements such as Al, Fe, and Pb. This study examines the leaching of the samples in HCl and H₂SO₄ under different conditions with the aim of obtaining a solution with a high concentration and high leaching efficiency of zinc. The L/S ratio of 3, 4 M H₂SO_4, and ambient temperature proved to be optimal for the leaching of the GFD residue, where 96.24% of zinc was leached out, which represents a zinc concentration of 136.532 g/L.