Layered perovskite-type oxides A2Ln2Ti3O10(A = Li, Na, K; Ln = La, Nd) prepared by solid-phase synthesis and their hydrated forms were characterized by the methods of TGA, XRD, and by UV-Vis...

A layered perovskite-type oxide intercalated with n-butylamine is reported as an efficient photocatalyst for hydrogen production from aqueous solutions of alcohols for the first time. The hybrid photocatalyst H₂Nd₂Ti₃O₁₀×BuNH₂ was synthesized by solid-state ceramic method followed by protonation, intercalation of methylamine and subsequent substitution by n-butylamine. The product was characterized by powder XRD, TGA, STA-MS, DRS, IR, and Raman spectroscopy, CHN analysis, SEM. Intercalation of n-butylamine caused a dramatic increase in photocatalytic activity of H₂Nd₂Ti₃O₁₀ in the reaction of hydrogen evolution from aqueous solutions of methanol, ethanol, and n-butanol under UV radiation. While the non-intercalated Pt-loaded H₂Nd₂Ti₃O₁₀ showed a maximum quantum efficiency of only 2% in the 220–340 nm range, the efficiency for hybrid samples reached 23% under the same conditions and after variation of experimental parameters even 52% efficiency was achieved. This effect may be associated with the significant expansion of the interlayer space, which is considered as a separate reaction zone.

A series of hybrid inorganic–organic niobates HCa₂Nb₃O₁₀×ROH, containing n-alkoxy groups of primary alcohols (R = Me, Et, Pr, Bu, Hx, and Dc) grafted in the interlayer space, has been studied for the first time in relation to photocatalytic hydrogen generation from a model 1 mol % aqueous solution of methanol under ultraviolet irradiation. Photocatalytic activity was measured both for bare samples and for their composites with Pt nanoparticles as a cocatalyst. The advanced measurement scheme allowed monitoring the volume concentration of a sample in a suspension during the experiment, its pH, and possible exfoliation of layered compounds into nanolayers. In the series of n-alkoxy derivatives, the maximum rate of hydrogen evolution was achieved over a Pt-loaded ethoxy derivative HCa₂Nb₃O₁₀×EtOH/Pt. Its apparent quantum efficiency of 20.6% in the 220–350 nm range was found not to be caused by changes in the light absorption region or specific surface area upon ethanol grafting. Moreover, the amounts of hydrogen released during the measurements significantly exceeded those of interlayer organic components, indicating that hydrogen is generated from the reaction solution rather than from the hybrid material.

Two series of hybrid inorganic-organic derivatives, obtained via the modification of protonated Ruddlesden–Popper phases H₂Ln₂Ti₃O₁₀ (Ln = La, Nd) with intercalated n-alkylamines and grafted n-alkoxy groups, have been systematically investigated in relation to photocatalytic hydrogen production from a model of 1 mol % aqueous solution of methanol for the first time. Photocatalytic measurements were performed both for bare samples and for their composites with Pt nanoparticles as a cocatalyst using an advanced scheme, including dark stages, monitoring of the volume concentration of the sample in the reaction suspension during the experiment, shifts of its pH and possible exfoliation of layered compounds into nanolayers. It was found that the incorporation of organic components into the interlayer space of the titanates increases their photocatalytic activity up to 117 times compared with that of the initial compounds. Additional platinization of the hybrid samples’ surface allowed for achieving apparent quantum efficiency of hydrogen evolution of more than 40%. It was established that the photocatalytic activity of the hybrid samples correlates with the hydration degree of their interlayer space, which is considered a separate reaction zone in photocatalysis, and that hydrogen indeed generates from the aqueous methanol solution rather than from organic components of the derivatives.

The layered double hydroxides (LDHs) of transition metals are of great interest as building blocks for the creation of composite photocatalytic materials for hydrogen production, environmental remediation and other applications. However, the synthesis of most LDHs is reported only by the conventional coprecipitation method, which makes it difficult to control the catalyst’s crystallinity. In the present study, ZnCr- and NiCr-LDHs have been successfully prepared using a facile hydrothermal approach. Varying the hydrothermal synthesis conditions allowed us to obtain target products with a controllable crystallite size in the range of 2–26 nm and a specific surface area of 45–83 m²∙g⁻¹. The LDHs synthesized were investigated as photocatalysts of hydrogen generation from aqueous methanol. It was revealed that the photocatalytic activity of ZnCr-LDH samples grows monotonically with the increase in their average crystallite size, while that of NiCr-LDH ones reaches a maximum with intermediate-sized crystallites and then decreases due to the specific surface area reduction. The concentration dependence of the hydrogen evolution activity is generally consistent with the standard Langmuir–Hinshelwood model for heterogeneous catalysis. At a methanol content of 50 mol. %, the rate of hydrogen generation over ZnCr- and NiCr-LDHs reaches 88 and 41 μmol∙h⁻¹∙g⁻¹, respectively. The hydrothermally synthesized LDHs with enhanced crystallinity may be of interest for further fabrication of their nanosheets being promising components of new composite photocatalysts.