Two series of hybrid inorganic-organic derivatives, obtained via the modification of protonated Ruddlesden–Popper phases H₂Ln₂Ti₃O₁₀ (Ln = La, Nd) with intercalated n-alkylamines and grafted n-alkoxy groups, have been systematically investigated in relation to photocatalytic hydrogen production from a model of 1 mol % aqueous solution of methanol for the first time. Photocatalytic measurements were performed both for bare samples and for their composites with Pt nanoparticles as a cocatalyst using an advanced scheme, including dark stages, monitoring of the volume concentration of the sample in the reaction suspension during the experiment, shifts of its pH and possible exfoliation of layered compounds into nanolayers. It was found that the incorporation of organic components into the interlayer space of the titanates increases their photocatalytic activity up to 117 times compared with that of the initial compounds. Additional platinization of the hybrid samples’ surface allowed for achieving apparent quantum efficiency of hydrogen evolution of more than 40%. It was established that the photocatalytic activity of the hybrid samples correlates with the hydration degree of their interlayer space, which is considered a separate reaction zone in photocatalysis, and that hydrogen indeed generates from the aqueous methanol solution rather than from organic components of the derivatives.

Aluminum-based metallic matrix composites reinforced by carbon nanofibers (CNFs) are important precursors for development of new light and ultralight materials with enhanced properties and high specific characteristics. In the present work, powder metallurgy technique was applied for production of composites based on reinforcement of aluminum matrices by CNFs of different concentrations (0~2.5 wt%). CNFs were produced by chemical vapor deposition (CVD) and mechanical activation. We determined that in situ synthesis of carbon nanostructures with subsequent mechanic activation provides satisfactory distribution of nanofibers and homogeneous composite microstructure. Introduction of 1 vol% of flux (0.25 NaCl + 0.25 KCl + 0.5 CaF₂) during mechanic activation helps to reduce the strength of the contacts between the particles. Additionally, better reinforcement of alumina particles and strengthening the bond between CNFs and aluminum are observed due to alumina film removal. Introduction of pure aluminum into mechanically alloyed powder provides the possibility to control composite durability, plasticity and thermal conductivity.