Silver diamine nitrate (SDN) is expected to help control caries similar to silver diamine fluoride (SDF). The aim of this study was to determine the mineral precipitation in demineralized dentin and the cytotoxicity of SDN and SDF to dental pulp cells. Demineralized dentin specimens were prepared, and SDF, SDN, or water (control) was applied. The specimens were then remineralized in simulated body fluid for 2 weeks. The mineral precipitation in the specimens was examined using FTIR-ATR, SEM-EDX, and synchrotron radiation X-ray tomographic microscopy (SRXTM). Additionally, the cytotoxicity of SDF and SDN to human dental pulp stem cells was analyzed using an MTT assay. The increase in FTIR spectra attributable to apatite formation in demineralized dentin in the SDF group was significantly higher compared to the SDN and control groups (p < 0.05). Dentinal tubule occlusion by the precipitation of silver salts was detected in both SDF and SDN groups. The mineral density as shown in SRXTM images and cytotoxicity of both SDN and SDF groups were comparable (p > 0.05). In conclusion, SDF demonstrated superior in vitro apatite formation compared to SDN. However, the degree of mineral precipitation and cytotoxic effects of both were similar.

The global population is growing older and entering an aging society. Aging results in severe tissue disorder and organ dysfunction. Bone-related injuries are particularly significant. The need for alternative bone replacement materials for human implants has grown over the past few decades. Alginate has the potential for use as a cell scaffold for bone tissue engineering due to its high bio-compatibility. To improve the bioactivity of alginate scaffolds, zinc- and strontium-containing sol-gel-derived bioactive glass nanoparticles (Zn-Sr-BGNPs) with sizes ranging from 100 to l40 nm were incorporated. Zn-Sr-BGNPs synthesized through the sol-gel process have a high sur-face-to-volume ratio, homogeneity, and purity, resulting in faster degradation. The therapeutic bivalent ions released from Zn-Sr-BGNPs strengthen the cell scaffold and improve the stimulation of the production and development of bone cells. Zn-Sr-BGNPs with different Zn to Si nominal ratios of 0, 1, and 1.5 were mixed with alginate in this research. The ratio of Zn in Zn-Sr-BGNPs and the ratio of Zn-Sr-BGNPs in scaffolds impact the pore size, swelling, and biological properties of synthesized composite scaffolds. The surface area and pore volume of a 1:1 1Zn-Sr-BGNP:Alg composite scaffold were 22.58 m²/g and 0.055 cm³/g, respectively. The incorporation of Zn-Sr-BGNPs improved the mechanical performance of the scaffolds up to 4.73 ± 0.48 MPa. The swelling rate decreased slightly from 2.12 (pure Alg) to 1.50 (1Zn-Sr-BGNP:Alg (1:1)). The 1Zn-Sr-BGNP:Alg (1:1) composite scaffold promoted bioactivity through apatite layer formation, increased bone cell proliferation via the dissolution products released from the scaffold, enhanced calcium deposition, and facilitated cell attachment. Thus, 1Zn-Sr-BGNP:Alg (1:1) composite scaffold is proposed as a possible artificial bone scaffold in bone tissue regeneration.

The aim of this study was to prepare RMGICs for pulp protection that contain polyacids functionalized with methacrylate groups (CMs) to enable light-activated polymerization without the need for toxic 2-hydroxyethyl methacrylate (HEMA) monomers. The effects of using CM liquids with 0 or 5 wt% HEMA on the physical/mechanical properties and cytotoxicity of the experimental RMGICs were assessed. Spherical pre-reacted glass fillers (SPG) were used as the powder phase. The experimental RMGICs were prepared by mixing SPG with CM liquid (0 wt% HEMA, F1) or CMH liquid (5 wt% HEMA, F2). Commercial materials (Vitrebond, VB; TheraCal LC, TC) were used for the comparisons. The degree of monomer conversion and fluoride release of both F1 and F2 were significantly lower than those of VB. F1 showed comparable biaxial flexural strength with VB but higher strength than TC. The dimensional stability (mass/volume changes) of the experimental materials was comparable with that of the commercial materials. F1 and F2 exhibited higher Sr/Ca ion release and relative cell viability than VB. The use of CMH liquid reduced the strength but enhanced the fluoride release of the experimental RMGICs. In conclusion, the experimental RMGICs showed comparable strength but lower cytotoxicity compared to the commercial RMGICs. These novel materials could be used as alternative materials for pulp protection.