In this work, we investigate ethanol (EtOH)-sensing mechanisms of a ZnO nanorod (NRs)-based chemiresistor using a near-ambient-pressure X-ray photoelectron spectroscopy (NAP-XPS). First, the ZnO NRs-based sensor was constructed, showing good performance on interaction with 100 ppm of EtOH in the ambient air at 327 °C. Then, the same ZnO NRs film was investigated by NAP-XPS in the presence of 1 mbar oxygen, simulating the ambient air atmosphere and O₂/EtOH mixture at the same temperature. The partial pressure of EtOH was 0.1 mbar, which corresponded to the partial pressure of 100 ppm of analytes in the ambient air. To better understand the EtOH-sensing mechanism, the NAP-XPS spectra were also studied on exposure to O₂/EtOH/H₂O and O₂/MeCHO (MeCHO = acetaldehyde) mixtures. Our results revealed that the reaction of EtOH with chemisorbed oxygen on the surface of ZnO NRs follows the acetaldehyde pathway. It was also demonstrated that, during the sensing process, the surface becomes contaminated by different products of MeCHO decomposition, which decreases dc-sensor performance. However, the ac performance does not seem to be affected by this phenomenon.

In this work, we present a complex study of photoregeneration of a zinc phthalocyanine (ZnPc) sensor by illumination from light-emitting diodes (LEDs). It includes an investigation of photoregeneration effectivity for various wavelengths (412–723 nm) of incident light carried out at sensor operating temperatures of 55 °C. It is demonstrated that the efficiency of photoregeneration is increasing with a decrease in the light wavelength. In the region of longer wavelengths (723–630 nm), the regeneration degree (RD) was low and ranged from 12% to 15%. In the region of shorter wavelengths (518–412 nm), the RD rose from 35% for 518 nm to 94% for 412 nm. The efficiency of photoregeneration is also shown to be higher in comparison with the temperature regeneration efficiency. In order to understand the chemism of photoregeneration processes, the electrical measurements are supplemented with Raman and near-ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) studies. The spectroscopic results showed that nitrogen dioxide bonds to the Zn atom in ZnPc in the form of NO₂⁻ and NO⁻, i.e., partial decomposition of NO₂ molecules occurs during the interaction with the surface. NAP-XPS spectra proved that light illumination of the ZnPc surface is essential for almost complete desorption of NO_x species. At the same time, it is demonstrated that in case of long-time exposure or exposure of a ZnPc chemiresistor with a high concentration of NO₂, the oxygen, released due to the NO₂ decomposition, slowly but irreversibly oxidizes the layer. This oxidation process is most probably responsible for the sensor deactivation observed in sensor experiments with high NO₂ concentrations. Based on these studies, the mechanism of nitrogen dioxide interaction with zinc phthalocyanine both under LED illumination and in dark conditions is proposed, and a special method for the sensor operation called “constant exposure dose” is established.