In this work, we investigate ethanol (EtOH)-sensing mechanisms of a ZnO nanorod (NRs)-based chemiresistor using a near-ambient-pressure X-ray photoelectron spectroscopy (NAP-XPS). First, the ZnO NRs-based sensor was constructed, showing good performance on interaction with 100 ppm of EtOH in the ambient air at 327 °C. Then, the same ZnO NRs film was investigated by NAP-XPS in the presence of 1 mbar oxygen, simulating the ambient air atmosphere and O₂/EtOH mixture at the same temperature. The partial pressure of EtOH was 0.1 mbar, which corresponded to the partial pressure of 100 ppm of analytes in the ambient air. To better understand the EtOH-sensing mechanism, the NAP-XPS spectra were also studied on exposure to O₂/EtOH/H₂O and O₂/MeCHO (MeCHO = acetaldehyde) mixtures. Our results revealed that the reaction of EtOH with chemisorbed oxygen on the surface of ZnO NRs follows the acetaldehyde pathway. It was also demonstrated that, during the sensing process, the surface becomes contaminated by different products of MeCHO decomposition, which decreases dc-sensor performance. However, the ac performance does not seem to be affected by this phenomenon.

The resolution of a quartz crystal microbalance (QCM) is particularly crucial for gas sensor applications where low concentrations are detected. This resolution can be improved by increasing the effective surface of QCM electrodes and, thereby, enhancing their sensitivity. For this purpose, various researchers have investigated the use of micro-structured materials with promising results. Herein, we propose the use of easy-to-manufacture metal blacks that are highly structured even on a nanoscale level and thus provide more bonding sites for gas analytes. Two different black metals with thicknesses of 280 nm, black aluminum (B-Al) and black gold (B-Au), were deposited onto the sensor surface to improve the sensitivity following the Sauerbrey equation. Both layers present a high surface roughness due to their cauliflower morphology structure. A high response (i.e., resonant frequency shift) of these QCM sensors coated with a black metal layer was obtained. Two gaseous analytes, H₂O vapor and EtOH vapor, at different concentrations, are tested, and a distinct improvement of sensitivity is observed for the QCM sensors coated with a black metal layer compared to the blank ones, without strong side effects on resonance frequency stability or mechanical quality factor. An approximately 10 times higher sensitivity to EtOH gas is reported for the QCM coated with a black gold layer compared to the blank QCM sensor.

In this work, we present a complex study of photoregeneration of a zinc phthalocyanine (ZnPc) sensor by illumination from light-emitting diodes (LEDs). It includes an investigation of photoregeneration effectivity for various wavelengths (412–723 nm) of incident light carried out at sensor operating temperatures of 55 °C. It is demonstrated that the efficiency of photoregeneration is increasing with a decrease in the light wavelength. In the region of longer wavelengths (723–630 nm), the regeneration degree (RD) was low and ranged from 12% to 15%. In the region of shorter wavelengths (518–412 nm), the RD rose from 35% for 518 nm to 94% for 412 nm. The efficiency of photoregeneration is also shown to be higher in comparison with the temperature regeneration efficiency. In order to understand the chemism of photoregeneration processes, the electrical measurements are supplemented with Raman and near-ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) studies. The spectroscopic results showed that nitrogen dioxide bonds to the Zn atom in ZnPc in the form of NO₂⁻ and NO⁻, i.e., partial decomposition of NO₂ molecules occurs during the interaction with the surface. NAP-XPS spectra proved that light illumination of the ZnPc surface is essential for almost complete desorption of NO_x species. At the same time, it is demonstrated that in case of long-time exposure or exposure of a ZnPc chemiresistor with a high concentration of NO₂, the oxygen, released due to the NO₂ decomposition, slowly but irreversibly oxidizes the layer. This oxidation process is most probably responsible for the sensor deactivation observed in sensor experiments with high NO₂ concentrations. Based on these studies, the mechanism of nitrogen dioxide interaction with zinc phthalocyanine both under LED illumination and in dark conditions is proposed, and a special method for the sensor operation called “constant exposure dose” is established.

Chemiresistors based on thin films of the Li-doped CuO–TiO₂ heterojunctions were synthesized by a 2-step method: (i) repeated ion beam sputtering of the building elements (on the Si substrates and multisensor platforms); and (ii) thermal annealing in flowing air. The structure and composition of the films were analyzed by several methods: Rutherford Backscattering (RBS), Neutron Depth Profiling (NDP), Secondary Ion Mass Spectrometry (SIMS), and Atomic Force Microscopy (AFM), and their sensitivity to gaseous analytes was evaluated using a specific lab-made device operating in a continuous gas flow mode. The obtained results showed that the Li doping significantly increased the sensitivity of the sensors to oxidizing gases, such as NO₂, O₃, and Cl₂, but not to reducing H₂. The sensing response of the CuO–TiO₂–Li chemiresistors improved with increasing Li content. For the best sensors with about 15% Li atoms, the detection limits were as follows: NO₂ → 0.5 ppm, O₃ → 10 ppb, and Cl₂ → 0.1 ppm. The Li-doped sensors showed excellent sensing performance at a lower operating temperature (200 °C); however, even though their response time was only a few minutes, their recovery was slow (up to a few hours) and incomplete.