The research into the road performance of coal gangue is of great significance for the consumption of coal gangue and reducing pollution. In this paper, the coal gangues were prepared by separation and crushing processes, and their gradations were also optimized. Aiming to identify the possible problems of coal gangue as a pavement base, an unconfined compressive strength test, a splitting test, a freeze–thaw test, and a drying shrinkage test of cement stabilized gangue with varying cement amounts were carried out, and the test results were compared and analyzed. The test results showed that the maximum dry density and optimum moisture content (OMC) of the optimized cement stabilized gangue and cement stabilized macadam increased with cement content. The maximum dry density and OMC of cement stabilized macadam were larger than that of cement stabilized gangue with the same cement content. The optimized 7-day unconfined compressive strength of cement stabilized gangue can meet the requirements for a secondary and lower highway base and subbase. The OMC and cement content are the critical factors affecting the compressive strength loss rate of cement stabilized gangue after freeze–thaw cycles. The smaller the OMC of cement stabilized gangue and the larger the cement content, the lower the compressive strength loss rate. With an increase in cement content, the drying shrinkage strain of cement stabilized gangue increased. The results show that a cement content of 4% is optimal for the cement stabilized coal gangue, which can be used for the light traffic base and heavy traffic subbase of class II and below highways. It provides a basis, guide, and reference for the application of coal gangue materials in a high-grade highway base.

The high-temperature rheological properties of emulsified asphalt mastics have a significant impact on the service performance of cold recycled mixtures with asphalt emulsions. In this paper, a dynamic shear rheological (DSR) test and a multiple stress creep recovery (MSCR) test are carried out to analyze the influence of tunneling coal gangue powder (TCGP), portland cement (PC), limestone powder (LP), and four kinds of filler binder ratio (F/B) on the high-temperature rheological properties of emulsified asphalt mastics before and after rolling thin film oven test (RTFOT) ageing. Based on the principle of time–temperature equivalence and a viscoelasticity material model, the main curve of emulsified asphalt mastics under frequency scanning test is established, and the rheological properties of emulsified asphalt mastics in a wide frequency domain are analyzed. Finally, the grey entropy theory is used to quantitatively analyze the correlation between different high temperature performance evaluation indices of emulsified asphalt mastics. The results show that the RTFOT ageing process can significantly enhance the high temperature deformation resistance of emulsified asphalt residue and its mastics. The rutting factor (G*/sin $\delta$) of emulsified asphalt mastics increases exponentially with the increase of F/B, while the phase angle is less affected. TCGP mastics and PC mastics have better high temperature performances than those of LP mastics. The most suitable range of F/B is 0.9~1.2 when TCGP is used as the filler, and 1.2~1.5 when PC or LP is used as the filler. Grey entropy correlation analysis shows that there is a good correlation between the two evaluation systems of the DSR test and the MSCR test, and both can evaluate the high-temperature performance of emulsified asphalt mastics.