The present clinical trial was conducted to evaluate the clinical performance of the biomimetic, bilayered structure utilizing a fiber reinforced bulk fill resin composite with a nanohybrid capping layer, compared to incremental packing of nanohybrid resin composite, in deep proximal cavities in permanent molars. A total of 36 deep proximal cavities in vital molars were restored either with a bilayered structure of fiber reinforced composite resin as a dentine substitute and a capping layer of nanohybrid composite resin (n=18) or conventional, nanohybrid composite resin incrementation (n=18). The restorations were assessed over a period of 12 months using the modified USPHS criteria. The criteria evaluated were: fracture and retention, marginal integrity, marginal discoloration, anatomic form, proximal contact, surface texture, radiographic evaluation, postoperative sensitivity and secondary caries. There was no statistically or clinically significant difference between fiber-reinforced resin composite and conventional incremental resin composite. There was no risk for failure regarding all the evaluated modified USPHS criteria for both materials after 12 months (RR= 1(95% CI 0.0209 to 47.8503; P =1.0000)). The biomimetic approach utilizing a fiber reinforced resin composite dentine substitute showed a comparable clinical performance to nanohybrid resin composite incrementation. Bulk fill fiber reinforced resin composite is an efficient alternative in restoration of deep proximal cavities in posterior teeth. Further long-term studies are necessary to confirm these results.

Background: Tooth wear can have a multifactorial aetiology which requires thorough patient assessment and aesthetic management. Purpose: This case report discusses the management of a young, Egyptian swimmer complaining of tooth sensitivity associated with erosive tooth wear. Anterior teeth were restored using the injection molding technique, also known as the injectable composite resin technique, to overcome the patient's complaint and enhance the aesthetics of compromised anterior teeth. Patients and Methods: Thorough patient assessment was followed by impression taking, a diagnostic wax-up and intraoral mock-up fabrication for aesthetic, functional and biological verification. Upon the patient's agreement on the proposed treatment, an injection molding technique was carried out. Conclusion: The tooth loss pattern associated with erosive tooth wear in competitive swimmers showed a very characteristic presentation. Detailed patient history is imperative for successful assessment of the risk factors contributing to the condition and treatment planning in such cases. The use of injection molding technique for restoration of anterior teeth is a simple, straightforward and aesthetically pleasing alternative for patients with erosive tooth wear requiring direct composite veneers.

T, and Cochrane from 2010 to 2020. Only articles published in English were included. In vivo studies, involving human subjects in whom SAP was delivered, were included. Results: Eight hundred and sixty articles were identified from the search after excluding duplicates. Abstracts of articles were reviewed independently. Eight hundred and twenty-four articles were excluded after reading the abstracts. Full-text articles were retrieved for 36 relevant studies. After reviewing articles independently, 25 were excluded after full-text reading. Finally, 11 studies were selected based on the eligibility criteria. All 11 articles reviewed SAP, seven of them compared SAP to fluoride, one compared SAP to no treatment, and three were case series studies. Conclusion: For the treatment of early enamel lesions, non-classical remineralization using SAP whether used alone or in combination with fluoride showed a positive outcome that was superior to that of fluoride varnish. Future studies are speculated to show higher probability to detect a positive effect with SAP....

Fiber-reinforced composites (FRCs) are recognized for enhancing the fracture resistance of structurally compromised teeth. However, the optimal orientation and placement of fibers in direct resin composite restorations remain under debate. This study aimed to evaluate the fracture resistance of maxillary premolars with mesio-occluso-distal (MOD) cavities restored using polyethylene fibers with different placement techniques, compared to conventional incremental composite restoration. Methods: Sixty intact maxillary premolars were randomly assigned to six groups (n = 10). Group 1: intact teeth (positive control); Group 2: MOD cavity without restoration (negative control); Group 3: MOD cavity restored with nanohybrid composite using the incremental technique; Group 4: polyethylene fiber placed on the pulpal floor; Group 5: fiber placed circumferentially along cavity walls (wall-papering technique); Group 6: fiber placed buccolingually in an occlusal groove (occlusal splinting). Fracture resistance was assessed using a universal testing machine. Failure mode was also analyzed. Results: Group 6 (occlusal splinting) exhibited the highest fracture resistance (1137.72 ± 316.20 N), significantly exceeding Group 3 (546.93 ± 59.89 N) and other fiber-reinforced groups (p < 0.05). Failure mode analysis revealed no significant differences between the fiber-reinforced groups and the intact teeth. Group 6 also had the highest percentage of restorable fractures (90%). Conclusions: Incorporating polyethylene fibers, especially through occlusal splinting, significantly improves fracture resistance in MOD-restored maxillary premolars. This technique may offer a promising alternative to conventional composite restorations in structurally weakened posterior teeth.