A low cost, abundant, and renewable vegetable oil source has been gaining increasing attention due to its potential to be chemically modified to polyol and thence to become an alternative replacement for the petroleum-based polyol in polyurethane production. In this study, jatropha oil-based polyol (JOL) was synthesised from non-edible jatropha oil by a two steps process, namely epoxidation and oxirane ring opening. In the first step, the effect of the reaction temperature, the molar ratio of the oil double bond to formic acid, and the reaction time on the oxirane oxygen content (OOC) of the epoxidised jatropha oil (EJO) were investigated. It was found that 4.3% OOC could be achieved with a molar ratio of 1:0.6, a reaction temperature of 60 °C, and 4 h of reaction. Consequently, a series of polyols with hydroxyl numbers in the range of 138–217 mgKOH/g were produced by oxirane ring opening of EJOs, and the physicochemical and rheological properties were studied. Both the EJOs and the JOLs are liquid and have a number average molecular weight (M_n) in the range of 834 to 1457 g/mol and 1349 to 2129 g/mol, respectively. The JOLs exhibited Newtonian behaviour, with a low viscosity of 430–970 mPas. Finally, the JOL with a hydroxyl number of 161 mgKOH/g was further used to synthesise aqueous polyurethane dispersion, and the urethane formation was successfully monitored by Fourier Transform Infrared (FTIR).

Nowadays, there is a significant trend away from solvent-based polyurethane systems towards waterborne polyurethane dispersions due to government regulations requiring manufacturers to lower total volatile organic compounds, as well as consumer preference for more environmentally friendly products. In this work, a renewable vegetable oil-based polyol derived from jatropha oil was polymerized with isophorone diisocyanate and dimethylol propionic acid to produce anionic waterborne polyurethane dispersion. Free standing films with up to 62 wt.% bio-based content were successfully produced after evaporation of water from the jatropha oil-based waterborne polyurethane (JPU) dispersion, which indicated good film formation. The chemical and thermo-mechanical properties of the JPU films were characterized. By increasing the OH numbers of polyol from 161 mgKOH/g to 217 mgKOH/g, the crosslinking density of the JPU was significantly increased, which lead to a better storage modulus and improved hydrophobicity. Overall, JPU produced from polyol having OH number of 217 mgKOH/g appears to be a promising product for application as a binder for wood and decorative coatings.

Purpose: This paper aims to demonstrate the synthesis of polyesterification reaction of non-edible jatropha seed oil (JO) and acrylic acid, which leads to the production of acrylated epoxidised-based resin. To understand the physico-chemical characteristics when synthesis the JO-based epoxy acrylate, the effect of temperature on the reaction, concentration of acrylic acid and role of catalyst on reaction time and acid value were studied. Design/methodology/approach: First, the double bond in JO was functionalised by epoxidation using the solvent-free performic method. The subsequent process was acrylation with acrylic acid using the base catalyst triethylamine and 4-methoxyphenol as an inhibitor respectively. The physico-chemical characteristics during the synthesis of the epoxy acrylate such as acid value was monitored and analysed. The formation of the epoxy and acrylate group was confirmed by a Fourier transform infrared spectroscopy spectra analysis and nuclear magnetic resonance analysis. Findings: The optimum reaction condition was achieved at a ratio of epoxidised JO to acrylic acid of 1:1.5 and the reaction temperature of 110°C. This was indicated by the acid value reduction from 86 to 15 mg KOH/g sample at 6 hours. Practical implications: The JO-based epoxy acrylate synthesised has a potential to be used in formulations the prepolymer resin for UV curable coating applications. The JO which is from natural resources and is sustainable raw materials that possible reduce the dependency on petroleum-based coating. Originality/value: The epoxidised jatropha seed oil epoxy acrylate was synthesised, as a new type of oligomer resin that contains a reactive acrylate group, which can be alternative to petroleum-based coating and can used further in the formulation of the radiation curable coating.

This research aims to investigate the effect of crude palm oil (CPO) as a plasticizer in polypropylene blown film on thermal and dynamic mechanical properties. Polypropylene (PP) was blended with 1, 3, and 5% of CPO using a twin screw extruder. The extruded samples were blown using the blown thin film technique. The samples were analyzed using dynamic mechanical analysis (DMA), differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). From the dynamic mechanical analysis, the storage modulus and loss modulus for PP presented decreasing pattern about 3–5% due to the action of CPO as plasticizer which introduced free volume and enabled the polyolefins chains to deform more easily. The glass transition temperatures (Tg) of PP were found being shifted to lower temperature from 10 to 1 °C with the increasing CPO content. The fraction of crystallization was determined using DSC. The thermogravimetric analysis (TGA) results showed that the incorporation of CPO as plasticizer showed a small increased effect in the thermal stability for PP. These findings have contributed new knowledge to the additives area and give important implications for designing and manufacturing polymer packaging materials.