Aluminophosphate glasses from the Li ₂ O-BaO-Al ₂ O ₃ -P ₂ O ₅ system with the addition of nonmagnetic and paramagnetic rare earth ions, were prepared using a wet nonconventional method to process the raw materials, followed by a melting–quenching procedure. The glasses obtained were characterized with respect to their magnetic and magneto-optical properties using superconducting quantum interference device magnetometry and spectroscopic ellipsometry. The assumption of a linear dependence of the Verdet constant on the magnetic susceptibility, with a proportionality constant dependent on the type of vitreous matrix and doping ion, is critically discussed. The diamagnetic and paramagnetic contributions to the Faraday rotation were separately analyzed and specific designs for optimal active and passive elements are proposed.

Durable biocompatible metal vascular implants are still one of the significant challenges of contemporary medicine. This work presents the preparation of ferromagnetic biomaterials with shape memory in metal strips based on FePd (30 at% Pd) that is either not doped or doped with Ga and Mn, coated with poly(benzofuran-co-arylacetic acid) or polyglutamic acid. The coating of the metal strips with polymers was achieved after the metal surface had been previously treated with open-air cold plasma. The final functionalization was performed to induce anti-thrombogenic/thrombolytic properties in the resulting materials. SEM-EDX microscopy and X-ray photoelectron microscopy (XPS) determined the morphology and composition of the metal strips covered with polymers. In vitro tests of standardized thromboplastin time (PTT) and prothrombin time (PT) were performed to evaluate the thrombogenicity of these biofunctionalized materials for future possible monitoring of the implant in patients.

Shape memory alloys, especially ferromagnetic shape memory alloys, are interesting new materials for the manufacturing of stents. Iron–palladium alloys in particular can be used to manufacture self-expanding temporary stents due to their optimum rate of degradation, which is between that of magnesium and pure iron, two metals commonly used in temporary stent research. In order to avoid blood clotting upon the introduction of the stent, they are often coated with anticoagulants. In this study, sulfated pectin, a heparin mimetic, was synthesized in different ways and used as coating on multiple iron–palladium alloys. The static and dynamic prothrombin time (PT) and activated partial thromboplastin time (APTT) of the prepared materials were compared to samples uncoated or coated with polyethylene glycol. While no large differences were observed in the prothrombin time measurements, the activated partial thromboplastin time increased significantly with all alloys coated with sulfated pectin. Aside from that, sulfated pectin synthesized by different methods also caused slight changes in the activated partial thromboplastin time. These findings show that iron–palladium alloys can be coated with anticoagulants to improve their utility as material for temporary stents. Sulfated pectin was characterized by nuclear magnetic resonance (NMR) and Fourier-transform infrared (FTIR) spectroscopy, and the coated alloys by scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX).

The influence of processing on the martensitic transformation and related magnetic properties of the Ni₅₅Fe₁₈Nd₂Ga₂₅ ferromagnetic shape memory alloy, as bulk and ribbons prepared by the melt spinning method and subjected to different thermal treatments, is investigated. Structural, calorimetric, and magnetic characterizations are performed. Thermal treatment at 1173 K induces a decrease in both the Curie and the martensitic transformation temperatures, while a treatment at 673 K produces the structural ordering of the ribbons, hence an increase in T_C. A maximum value of the magnetic entropy variation of −5.41 J/kgK was recorded at 310 K for the as quenched ribbons. The evaluation of the magnetoresistive effect shows a remarkable value of −13.5% at 275 K on the bulk sample, which is much higher than in the ribbons.