Poly(ethylene succinate) (PES) is one of the most promising biodegradable and biocompatible polyesters and is widely used in different biomedical applications. However, little information is available on its solubility and precipitation properties, despite that these solution behavior properties affect its applicability. In order to systematically study these effects, biodegradable and biocompatible poly(ethylene succinate) (PES) was synthesized using ethylene glycol and succinic acid monomers with an equimolar ratio. Despite the optimized reaction temperature (T = 185 °C) of the direct condensation polymerization, relatively low molecular mass values were achieved without using a catalyst, and the M_n was adjustable with the reaction time (40–100 min) in the range of ~850 and ~1300 Da. The obtained crude products were purified by precipitation from THF (“good” solvent) with excess of methanol (“bad” solvent). The solvents for PES oligomers purification were chosen according to the calculated values of solubility parameters by different approaches (Fedors, Hoy and Hoftyzer-van Krevelen). The theta-solvent composition of the PES solution was 0.3 v/v% water and 0.7 v/v% DMSO in this binary mixture. These measurements were also allowed to determine important parameters such as the coefficients A (=0.67) and B (=3.69 × 10⁴) from the Schulz equation, or the K_η (=8.22 × 10⁻²) and α (=0.52) constants from the Kuhn–Mark–Houwink equation. Hopefully, the prepared PES with different molecular weights is a promising candidate for biomedical applications and the reported data and constants are useful for other researchers who work with this promising polyester.

Herein we present the synthesis of a polymeric prodrug nanomaterial capable of spontaneous, self-assembled nanoparticle formation and of the conjugation (encapsulation) of drugs with amino and/or carboxyl and/or hydroxyl groups via ester and/or amide linkage. Mitomycin C (MMC) a versatile drug with antibiotic, antibacterial and antineoplastic properties, was used to prove this concept. The in vitro drug release experiments showed a fast release for the pure MMC (k = 49.59 h⁻ⁿ); however, a significantly lower MMC dissolution rate (k = 2.25, 1.46, and 1.35 h⁻ⁿ) was obtained for the nanoparticles with increased cross-link density (3, 10, 21%). The successful modification and conjugation reactions were confirmed using FTIR and EDX measurements, while the mucoadhesive properties of the self-assembled particles synthesized in a simple one-pot reaction were proved by rheological measurement. The prepared biocompatible polymeric prodrugs are very promising and applicable as a drug delivery system (DDS) and useful in the area of cancer treatment.

A two-component injectable hydrogel was suitably prepared for the encapsulation and prolonged release of tilorone which is an antimuscular atrophy drug. The rapid (7–45 s, depending on the polymer concentration) in situ solidifications of the hydrogel were evoked by the evolving Schiff-base bonds between the aldehyde groups of modified PVA (4-formyl benzoate PVA, PVA-CHO, 5.9 mol% functionalization degree) and the amino groups of 3-mercaptopropionate chitosan (CHIT-SH). The successful modification of the initial polymers was confirmed by both FTIR and NMR measurements; moreover, a new peak appeared in the FTIR spectrum of the 10% w/v PVA-CHO/CHIT-SH hydrogel at 1647 cm⁻¹, indicating the formation of a Schiff base (–CH=N–) and confirming the interaction between the NH₂ groups of CHIT–SH and the CHO groups of PVA-CHO for the formation of the dynamic hydrogel. The reaction between the NH₂ and CHO groups of the modified biopolymers resulted in a significant increase in the hydrogel’s viscosity which was more than one thousand times greater (9800 mPa·s) than that of the used polymer solutions, which have a viscosity of only 4.6 and 5.8 mPa·s, respectively. Furthermore, the initial chitosan was modified with mercaptopropionic acid (thiol content = 201.85 ± 12 µmol/g) to increase the mucoadhesive properties of the hydrogel. The thiolated chitosan showed a significant increase (~600 mN/mm) in adhesion to the pig intestinal membrane compared to the initial one (~300 mN/mm). The in vitro release of tilorone from the hydrogel was controlled with the crosslinking density/concentration of the hydrogel; the 10% w/v PVA-CHO/CHIT-SH hydrogel had the slowest releasing (21.7 h^−1/2) rate, while the 2% w/v PVA-CHO/CHIT-SH hydrogel had the fastest releasing rate (34.6 h^−1/2). Due to the characteristics of these hydrogels, their future uses include tissue regeneration scaffolds, wound dressings for skin injuries, and injectable or in situ forming drug delivery systems. Eventually, we hope that the developed hydrogel will be useful in the local treatment of muscle atrophy, such as laryngotracheal atrophy.

With the increasing demand for liquid manipulation and microfluidic techniques, surfaces with real-time tunable wetting properties are becoming the focus of materials science researches. In this study, we present a simple preparation method for a 0.5–4 µm carbonyl iron (carbonyl Fe) loaded polydimethylsiloxane (PDMS)-based magnetic composite coating with magnetic field-tailored wetting properties. Moreover, the embedded 6.3–16.7 wt.% Ag-TiO₂ plasmonic photocatalyst (d~50 nm) content provides additional visible light photoreactivity to the external stimuli-responsive composite grass surfaces, while the efficiency of this photocatalytic behavior also turned out to be dependent on the external magnetic field. The inclusion of the photocatalyst introduced hierarchical surface roughness to the micro-grass, resulting in the broadening of the achievable contact and sliding angle ranges. The photocatalyst-infused coatings are also capable of catching and releasing water droplets, which alongside their multifunctional (photocatalytic activity and tunable wetting characteristics) nature makes surfaces of this kind the novel sophisticated tools of liquid manipulation.