Nanoindentation (NI) is a contact method to investigate localized micromechanical properties of materials, whereby NI of semi-crystalline polymers is challenging. The influence of morphological structures such as spherulites or crystal-lamellae on localized NI depth-force behavior is discussed controversially in literature. Hence, the main objective of this study is to determine the influence of crystalline zones on NI results. Polyoxymethylene (POM) exhibits high crystallinity with the spherulitic structure on the micrometer scale and was therefore chosen to proof the influence of spherulite distribution on NI results concerning modulus. Furthermore, the correspondence between the mean elastic modulus from different NI experiments and macroscopic compression tests will be demonstrated. A POM tensile bar was investigated by NI with a large sphero-conical and a Berkovich indenter tip at different positions of its cross-section. Here, it was found that regions at the edge of the sample have a lower elastic modulus than regions in the middle of the cross-section. This agrees well with polarized light microscopy results, which reveal a skin layer with less crystallinity close to the sample edge. Therefore, the NI measurements in this edge zone result in a lower elastic modulus compared to the more crystalline middle of the cross-section. In summary, semi-crystallinity influences the NI results obtained for POM and the mean of the elastic modulus distribution over the cross-section of the POM sample is in good agreement with macroscopic compression test results.

In recent years, photovoltaic (PV) encapsulant films marketed as polyolefins (POs), more specifically as PO elastomers (POEs) and thermoplastic POs (TPOs), have gained significant market share and are projected to become the dominant encapsulation films by 2030. Relative to other industries, there are significant misconceptions about the term PO in the PV industry. Both in the scientific literature as well as in sales and advertising, the terms PO, POE, and TPO are often misused to describe the same type of material with comparable properties, while in reality these may each consist of separate material classes. This paper provides a comprehensive literature and market review, to showcase a broad range of PO and other ethylene copolymer encapsulants from recent studies, and discusses the materials' properties to clarify what constitutes a “polyolefin.” In addition, to promote a clearer comparison of encapsulant properties, we propose a two‐dimensional taxonomy to categorize polymers used in module manufacturing, including POs. In terms of improving the reliability of solar PV modules, PO‐based encapsulants have several advantages (including lower water uptake and ion diffusion), but might come with disadvantages too, such as a more complex processing and a higher sensitivity to the storage conditions and shelf life. All this might prospectively impact adhesion properties of the encapsulant to other materials' interfaces (glass, cells etc.) and end‐product quality. Because the track record of field‐deployed PV modules containing PO encapsulants is also limited, we hope to contribute to better material understanding and precision in communication in PV to secure quality.

The lifetime of industrial polymer products is in many cases limited by aging. Therefore, it is necessary to develop a fast and sensitive method to detect polymer aging at an early stage. A commercially available 50-µm-thick and transparent polyethylene terephtalate (PET) film was aged under different artificial conditions, and the evolution of mechanical properties with increasing aging time was investigated via nanoindentation (NI) and tensile testing. Chemical aging was studied with gel permeation chromatography (GPC), and physical aging was monitored by the first heating of differential scanning calorimetry. NI data evaluated with the method of Oliver and Pharr was compared to tensile test data with good agreement between the results on the macro- and nanoscales. Furthermore, a correlation between NI creep data and GPC data was obtained, which indicates that the aging of the PET films primarily originated from chemical aging. This study states that NI is an appropriate method to determine degradation of PET at an early stage.

The power degradation and failure of photovoltaic (PV) modules can be caused by changes in the mechanical properties of the polymeric components during the module lifetime. This paper introduces instrumented nanoindentation as a method to investigate the mechanical properties of module materials such as polymeric encapsulants. To this end, nanoindentation tests were carried out on ethylene vinyl acetate (EVA) surfaces, which have been separated from the glass panel. Two types of time-dependent indentation cycle modes, the time domain (creep mode) and frequency domain (dynamic mode) were performed to determine the viscoelastic behavior. For each mode, a corresponding model was applied to calculate the main mechanical properties. The general capability of nanoindentation as cross-linking determination method is investigated with the methodological advantages over bulk mechanical characterization methods. A large number of Glass/EVA/Backsheet laminates were built using different lamination conditions resulting in different degrees of curing. Both indentation modes indicate good modulus sensitivity for following the EVA crosslinking in its early stages but could not reliably differentiate between samples with higher EVA branching. Additional dynamic mechanical analysis (DMA) characterization was used as an established method to validate the indentation measurements. Both nanoindentation and DMA tensile mode produce similar quantitative viscoelastic responses, in the form of the damping factor parameter, demonstrated for three different frequencies at room temperature. A statistical study of the data reveals the advantages for the investigation of multilayer PV laminates by using nanoindenation as a surface method while also being applicable to field aged modules.