This paper aims to study the viability of conductive cement paste and conductive concrete with the hybrid addition of carbon nanotubes (CNT) and graphite powder (GP) as a self-heating material for heating, ice formation prevention and de-icing in pavements. Different heating tests, ice-preventing tests and de-icing tests were performed with cement paste and concrete specimens. Results confirm that the conductive cement composites studied, with the addition of 1% CNT + 5% GP, exhibited heating, de-icing and ice-prevention properties, when applying constant AC/DC voltages between the two end sides of each specimen, with relatively low energy consumption. The main contribution of this work is to achieve a sufficient conductivity level for the development of the heating and de-icing function using this hybrid addition in concrete, which has not been used so far, in order to be applied in real concrete structures.

In this study, CNTs and graphite have been incorporated to provide electrical conductivity and self-heating capacity by Joule effect to an epoxy matrix. Additionally, both types of fillers, with different morphology, surface area and aspect ratio, were simultaneously incorporated (hybrid CNTs and graphite addition) into the same epoxy matrix to evaluate the effect of the self-heating capacity of carbon materials-based resins on de-icing and ice-prevention capacity. The self-heating capacity by Joule effect and the thermal conductivity of the differently filled epoxy resin were evaluated for heating applications at room temperature and at low temperatures for de-icing and ice-prevention applications. The results show that the higher aspect ratio of the CNTs determined the higher electrical conductivity of the epoxy resin compared to that of the epoxy resin filled with graphite, but the 2D morphology of graphite produced the higher thermal conductivity of the filled epoxy resin. The presence of graphite enhanced the thermal stability of the filled epoxy resin, helping avoid its deformation produced by the softening of the epoxy resin (the higher the thermal conductivity, the higher the heat dissipation), but did not contribute to the self-heating by Joule effect. On the other hand, the feasibility of electrically conductive epoxy resins for de-icing and ice-prevention applications by Joule effect was demonstrated.

The thermal decomposition of a heat-not-burn (HNB) tobacco at four temperatures (250–400 °C) was studied via thermogravimetric analysis (TGA) and Multi-shot pyrolizer experiments (Py-GC/MS), and the effect of four potential additives, USY Beta and beta zeolites and Silica Lovel 6000 and SBA-15 silicates at three concentrations (5, 15 and 25% w/w) under an inert and oxidative atmosphere was analyzed. Different techniques were applied showing that the presence of the additives modifies the decomposition processes (TGA). Py-GC/MS showed that these tobaccos generate large amounts of Nicotine and Glycerine. Acid compounds are the most abundant compounds under an inert atmosphere, while Oxygenated compounds predominate under an oxidative atmosphere. In both atmospheres, Furans and Aromatics present in a significant abundance at high temperatures. The additives used reduce both the number and the concentration of most of the compounds generated, especially at high temperatures and concentrations. Moreover, SBA-15 shows good aptitudes to reduce the formation of some individual compounds included in the FDA’s HPHC list, such as Acetone and Acetaldehyde. Finally, smoking experiments corroborated that all additives produce marked reductions in TPM, i.e., the majority fraction obtained, and in practically all the compounds generated. Phenol, a toxicant compound that was detected in a significant amount, is also markedly reduced. SBA-15 is the material that presents a major reduction in the TPM and the principal compounds generated. These results may be of great interest for further reducing the toxicity of smoking this type of heat-not-burn tobacco product.