The demand for geopolymer materials is constantly growing. This, in turn, translates into an increasing number of studies aimed at developing new approaches to the methodology of geopolymer synthesis. The range of potential applications of geopolymers can be increased by improving the properties of the components. Future directions of studies on geopolymer materials aim at developing geopolymers showing excellent mechanical properties but also demonstrating significant improvement in thermal, magnetic, or sorption characteristics. Additionally, the current efforts focus not only on the materials’ properties but also on obtaining them as a result of environment-friendly approaches performed in line with circular economy assumptions. Scientists look for smart and economical solutions such that a small amount of the modifier will translate into a significant improvement in functional properties. Thus, special attention is paid to the application of nanomaterials. This article presents selected nanoparticles incorporated into geopolymer matrices, including carbon nanotubes, graphene, nanosilica, and titanium dioxide. The review was prepared employing scientific databases, with particular attention given to studies on geopolymer nanocomposites. The purpose of this review article is to discuss geopolymer nanocomposites in the context of a sustainable development approach. Importantly, the main focus is on the influence of these nanomaterials on the physicochemical properties of geopolymer nanocomposites. Such a combination of geopolymer technology and nanotechnology seems to be promising in terms of preparation of nanocomposites with a variety of potential uses.

The aim of the article is to analyze the structure and mechanical properties in terms of the cracking mechanics of geopolymer composites based on fly ash and river sand, as well as metakaolin and river sand with three types of reinforcement material: glass fiber, carbon fiber, and aramid fiber, in terms of their use in additive manufacturing. Geopolymer composites were reinforced with fibers in a volume ratio of 0.5%, 1.0%, and 2.0%. Subsequently, these samples were subjected to bending strength tests in accordance with the European standard EN 12390-3. The addition of fibers significantly improved the bending strength of all composites made of metakaolin and sand. The reinforcement with aramid fiber in the amount of 2.0% resulted in more than a 3-fold increase in strength compared to the reinforcement-free composites. An analysis of the morphology of the fibers was carried out on the basis of photos taken from an electron microscope. The correct addition of fibers changes the nature of the fracture from brittle to more ductile and reduces the number of cracks in the material.

In recent years, 3D concrete printing technology has been developing dynamically. Intensive research is still being carried out on the composition of the materials dedicated to innovative 3D printing solutions. Here, for the first time, concrete-geopolymer hybrids produced with 3D printing technology and dedicated environmentally friendly building construction are presented. The concrete-geopolymer hybrids consisting of 95% concrete and 5% geopolymer based on fly ash or metakaolin were compared to standard concrete. Moreover, 3D printed samples were compared with the samples of the same composition but prepared by the conventional method of casting into molds. The phase composition, water leachability, compressive, and flexural strength in the parallel and perpendicular directions to the printing direction, and fire resistance followed by compressive strength were evaluated. Concrete-geopolymer hybrids were shown to contain a lower content of hazardous compounds in leaches than concrete samples. The concentration of toxic metals did not exceed the limit values indicated in the Council Decision 2003/33/EC; therefore, the materials were classified as environmentally neutral. The different forms of Si/Al in fly ash and metakaolin resulted in the various potentials for geopolymerization processes, and finally influenced the densification of the hybrids and the potential for immobilization of toxic elements. Although the compressive strength of concrete was approximately 40% higher for cast samples than for 3D printed ones, for the hybrids, the trend was the opposite. The addition of fly ash to concrete resulted in a 20% higher compressive strength compared to an analogous hybrid containing the addition of metakaolin. The compressive strength was 7–10% higher provided the samples were tested in the parallel direction to the Z-axis of the printout. The sample compressive strength of 24–43 MPa decreased to 8–19 MPa after the fire resistance tests as a result of moisture evaporation, weight loss, thermal deformation, and crack development. Importantly, the residual compressive strength of the hybrid samples was 1.5- to 2- fold higher than the concrete samples. Therefore, it can be concluded that the addition of geopolymer to the concrete improved the fire resistance of the samples.

Construction and demolition waste (CDW) is the third-most abundant waste generated annually in the countries of the European Union. One of the alternatives to the use of these wastes is geopolymeric materials. Partial replacement of commonly used raw materials for the production of these materials can help reduce the number of landfills and the consumption of natural resources. In this study, the authors partially replaced metakaolin and fly ash with clay bricks and concrete debris. The research method in article is connected with analysis of microstructures and the mechanical and physical properties of the geopolymers. The results obtained show the possibility of manufacturing useful construction materials based on industrial byproducts (fly ash) and CDW. Compressive strength and flexural strength were, for samples containing metakaolin, 20.1 MPa and 5.3 MPa, respectively. Geopolymers containing fly ash displayed 19.7 MPa of compressive strength and 3.0 MPa of flexural strength. The results for both synthesized materials give them perspectives for future applications in the construction industry.

Two geopolymer foams were prepared from a thermally activated coal gangue containing kaolinite. As the foaming agent, aluminium powder and 36% hydrogen peroxide were used to obtain two levels of porosity. The materials’ high temperature performances were investigated: tensile and compressive strength evolution with temperature. This study shows that the mechanical performances of developed geopolymer foams are similar to foam concrete of the same apparent density. The geopolymer foams from coal gangue present stable mechanical performances up to 600 °C. When the glass transition temperature is achieved, sintering occurs and mechanical performance increases. SEM observations confirm the glass transition and densification of the matrix at temperatures above 800 °C. Moreover, the XRD measurements revealed a high amount of mullite that forms at 1000 °C that explained the observed strength increase. The synthesis of good-quality geopolymer foams from coal gangue and its application as a thermal barrier is feasible. The constant level of porosity and its stable character in the range of temperatures 20–1000 °C ensures stable thermal insulation parameters with increasing temperature, which is extremely important for fire protection.

Geopolymer materials are increasingly being considered as an alternative to environmentally damaging concrete based on Portland cement. The presented work analyzed waste from mines and waste incineration plants as potential precursors for producing geopolymer materials that could be used to make lightweight foamed geopolymers for insulation applications. The chemical and phase composition, radioactivity properties, and leachability of selected precursors were analyzed. Then, geopolymer materials were produced, and their strength properties were examined through compression and flexural tests. The results of the strength tests guided the material selection for foamed geopolymer materials. Next, geopolymer foams were foamed with hydrogen peroxide and aluminum powder. The produced foamed materials were subjected to strength and thermal conductivity tests. The results demonstrated the great potential of mine waste in the synthesis of geopolymers and the production of lightweight geopolymer foams with good insulating properties.