The study evaluated the possibility of using natural fibers as a reinforcement of bio-polyethylene. Flax, coconut, basalt fiber, and wood flour were used in the work. Strength tests like static tensile test, three-point flexural test, or impact strength showed a positive effect of reinforcing bio-polyethylene-based composites. The effect of water and thermal ageing on the mechanical behavior of composites was assessed. In order to analyze the structure, SEM microscope images were taken and the effect of natural fibers on the change in the nature of cracking of composites was presented. Composites with natural fibers at a content of 12% by weight, resulting in increase of strength and rigidity of materials. The greatest strengthening effect for natural fibers was obtained for the composite with basalt fibers.

This study investigated the influence of the steel and melamine fibers hybridization on the flexural and compressive strength of a fly ash-based geopolymer. The applied reinforcement reduced the geopolymer brittleness. Currently, there are several types of polymer fibers available on the market. However, the authors did not come across information on the use of melamine fibers in geopolymer composites. Two systems of reinforcement for the composites were investigated in this work. Reinforcement with a single type of fiber and a hybrid system, i.e., two types of fibers. Both systems strengthened the base material. The research results showed the addition of melamine fibers as well as steel fibers increased the compressive and flexural strength in comparison to the plain matrix. In the case of a hybrid system, the achieved results showed a synergistic effect of the introduced fibers, which provided better strength results in relation to composites reinforced with a single type of fiber in the same amount by weight.

This study aims to analyze strength properties and low-cycle dynamic tests of composite materials modified with glass and basalt fibers. Biopolyamide 4.10 was used as the matrix, and the fiber contents were 15, 30, and 50% by weight. Static tensile tests, impact tests, and determination of mechanical hysteresis loops were carried out as strength tests. The length of the fibers in the produced composites and their processing properties were determined. The composite materials were compared with commercially available glass fiber-reinforced composites with 30 and 50% fiber contents. The results showed that such composites can successfully replace composite materials based on petroleum-based polymeric materials, providing high strength properties and reducing the negative environmental impact by using renewable sources. Composites with 30% basalt fiber composition were characterized by higher tensile strength by about 60% compared to commercially available composites with 30% glass fiber composition and an almost doubly increased Young’s modulus. Increasing the content of basalt fibers to 50% results in a further increase in strength properties. Despite the lower tensile strength compared to polyamide 6 with 50% glass fiber content, basalt fibers provided an approximately 10% higher modulus of elasticity.

This paper presents the results of research on geopolymer composites based on fly ash with the addition of melamine fibers in amounts of 0.5%, 1% and 2% by weight and, for comparison, without the addition of fibers. The melamine fibers used in the tests retain their melamine resin properties by 100% and are characterized by excellent acoustic and thermal insulation as well as excellent filtration. In addition, these fibers are nonflammable, resistant to chemicals, resistant to UV radiation, characterized by high temperature resistance and, most importantly, do not show thermal-related shrinking, melting and dripping. This paper presents the results of density measurements, compressive and flexural strength as well as the results of the measurement of thermal radiation changes in samples subjected to a temperature of 600 °C. The results indicate that melamine fibers can be used as geopolymer reinforcement. The best result was achieved for 0.5% by weight amount of reinforcement, approximately 53 MPa, compared to 41 MPa for a pure matrix. In the case of flexural strength, the best results were obtained for the samples made of unreinforced geopolymer and samples with the addition of 0.5% by weight of melamine fibers, which were characterized by bending strength values above 9 MPa, amounting to 10.7 MPa and 9.3 MPa, respectively. The thermal radiation measurements and fire-jet test did not confirm the increasing thermal and fire resistance of the composites reinforced by melamine fiber.