The pulsed laser welding of Al ribbon to Cu sheet was investigated for the electrical interconnections in power electronic modules. The various experimental conditions with the different laser powers, scan speeds, and heat inputs were employed for obtaining the defect-free Al/Cu joints. During the Al/Cu laser welding, the intermetallic compounds were formed in the welding zone. An electron probe microanalyzer and transmission electron microscopy confirmed the phases of intermetallic compounds, which were found to be Al₄Cu₉, Al₂Cu, AlCu, etc. The computational fluid dynamics simulation revealed that the Marangoni effect induced the circulation of the molten pool, resulting in the mixture of Al and Cu and the formation of swirl-like structures at the Al/Cu joints. The tensile shear strengths and electrical resistances of the Al/Cu joints were measured, and they showed a strong correlation with the welding area. A decrease in mechanical strength and an increase in electrical resistance were measured with increasing the welding area of Al/Cu joints. Moreover, the process window for the defect-free Al/Cu joints was developed, and the experimental conditions for Al/Cu laser braze-welding were examined to minimize the intermetallic compounds formation at the Al/Cu joints.

In this study, the laser cutting characteristics were analyzed according to the shape of the back side of the specimen, and the laser cutting characteristics were compared according to the thickness of the edge (10 mm, 20 mm, and 30 mm). A Yb-YAG laser was used in this study, and the cutting target was STS304 with a thickness of 50 mm, and the cutting process was analyzed using a high-speed camera. In the experiment, it was found through image analysis that the cutting performance was excellent at 30 mm thickness of the edge. In order to analyze this reason, a thermal conduction analysis (numerical simulation) was performed, and it was confirmed that the thicker thickness of the edge caused a preheating effect during laser cutting due to a large amount of heat accumulation. This effect can be used as a reference for the initial processing state while cutting thick metals as it is a characteristic that has not been revealed before.

The autogenous manual gas tungsten arc welding (GTAW) process was used for cladding austenitic stainless steel 316L using a single pass with various contact tip-to-work distances (CTWDs). Immersion and electrochemical tests were used to evaluate the corrosion resistance of the welded specimens, and a microstructural analysis was conducted to investigate the chemical composition of the molten pool and the heat-affected zone of welding. The key findings of this study indicate that the corrosion resistance improved under a CTWD of 5 mm due to the optimal distribution of ferrite and a refined microstructure. Additionally, the highest hardness was observed in specimens with a CTWD of 3 mm, attributed to the increased ferrite content in the weld metal. As the CTWD increased, the ferrite fraction decreased, and the hardness also diminished. However, in the CTWD 7 mm case, the higher heat input influenced the microstructure and molten pool shape significantly through the Marangoni effect, resulting in a lower corrosion resistance. These results suggest that optimizing the CTWD can enhance the corrosion resistance of welded 316L stainless steel.

Laser shock peening creates compressive residual stress on the surface of the material, reducing stress corrosion cracking and increasing fatigue life. FE simulation of laser shock peening is an effective way to determine the mechanical effects on the material. In conventional FE simulations of laser shock peening, explicit analysis is used while pressure loads are applied and switched into implicit analysis to dissipate kinetic energy. In this study, static damping was adopted to dissipate kinetic energy without conversion into implicit analysis. Simulation of a single laser shock and multiple shocks was performed, and deformation and minimum principal stress were compared to evaluate the static damping effect. The history of the internal and kinetic energy were analyzed to compare the stabilization time depending on the damping value. Laser shock peening experiments were also performed on stainless steel 304 material. The residual stress of the specimen was measured by the hole drilling method and it was compared to the FE simulation result. The residual stress from the experiment and the simulation results showed similar distributions in the depth direction. Anisotropic residual stress distribution due to the laser path was observed in both results.