Alkali treatment is used for melt extrusion film formation with corn starch, but optimal conditions for this procedure are still unknown. In this study, the changes in properties and structure of high amylose corn starch (70%) films with different concentrations of sodium hydroxide (NaOH), prepared by melting extrusion, were investigated. With increasing sodium hydroxide concentrations, the tensile strength of the high-amylose starch film decreased gradually, while the elongation at break increased. The tensile strength of the high amylose starch (HAS) film with 2% NaOH-treatment was 10.03 MPa and its elongation at break was 40%. A 2% NaOH-treatment promoted the orderly rearrangement of starch molecules and formed an E_h-type crystal structure, which enlarged the spacing of the single helix structure, increased the molecular mobility of the starch, and slowed down the process of recrystallization; a 10% NaOH-treatment oxidized the hydroxyl groups of the high amylose corn starch during extrusion, formed a poly-carbonyl structure, and initiated the degradation and cross-linking of starch molecule chains.

Hydroxypropyl amylomaize starch (HPAS) films were prepared by hot press. The effects of initial pH of HPAS on the mechanical properties, molecular interaction, structure, and cross-linking degree of the resultant films were investigated. A weak acidic condition was suitable for cross-linking of citric acid and HPAS by reactive extrusion. The film of HPAS with an initial pH of 5.66 had the maximum tensile strength of 7.20 MPa and elongation-at-break of 94.53%, and the weight average molecular weight of HPAS increased to 4.17 × 10⁵ g/mol. An appropriate initial pH facilitated the formation of diester bonds between HPAS and citric acid during extrusion, but too low initial pH levels resulted in hydrolysis of starch molecules and reduced the mechanical properties.

The thermal stability and degradation kinetics of patulin (PAT, 10 μmol/L) in pH 3.5 of phosphoric-citric acid buffer solutions in the absence and presence of cysteine (CYS, 30 μmol/L) were investigated at temperatures ranging from 90 to 150 °C. The zero-, first-, and second-order models and the Weibull model were used to fit the degradation process of patulin. Both the first-order kinetic model and Weibull model better described the degradation of patulin in the presence of cysteine while it was complexed to simulate them in the absence of cysteine with various models at different temperatures based on the correlation coefficients (R² > 0.90). At the same reaction time, cysteine and temperature significantly affected the degradation efficiency of patulin in highly acidic conditions (p < 0.01). The rate constants (k_T) for patulin degradation with cysteine (0.0036–0.3200 μg/L·min) were far more than those of treatments without cysteine (0.0012–0.1614 μg/L·min), and the activation energy (E_a = 43.89 kJ/mol) was far less than that of treatment without cysteine (61.74 kJ/mol). Increasing temperature could obviously improve the degradation efficiency of patulin, regardless of the presence of cysteine. Thus, both cysteine and high temperature decreased the stability of patulin in highly acidic conditions and improved its degradation efficiency, which could be applied to guide the detoxification of patulin by cysteine in the juice processing industry.

The knowledge gained from starch-nanocomposite-film research has not been fully applied commercially because of the lack of appropriate industrial processing techniques for nanofillers and starch films. Three organically modified montmorillonites (OMMTs) were prepared using a semidry kneading method. The effects of the OMMTs on the structures and properties of starch nanocomposite films, prepared by extrusion blowing, were investigated. The X-ray diffraction (XRD) analysis results revealed that the OMMTs with various quaternary ammonium salts possessed differing layer structures and d-space values. The results of the XRD and Fourier-transform infrared spectroscopy (FT-IR) showed that the starch–OMMT interaction resulted in a structural change, namely the starch–OMMT films possessed a balanced exfoliated and intercalated nanostructure, while the starch–MMT film possessed an exfoliated nanostructure with non-intercalated montmorillonite (MMT). The results of the solid-state nuclear magnetic resonance (NMR) analysis suggested that the starch-OMMT nanocomposite possessed comparatively large quantities of single-helix structures and micro-ordered amorphous regions. The starch–OMMT films exhibited good tensile strength (TS) (maximum of 6.09 MPa) and water barrier properties (minimum of 3.48 × 10⁻¹⁰ g·m·m⁻²·s⁻¹·Pa⁻¹). This study indicates that the addition of OMMTs is a promising strategy to improve the properties of starch films.