The present study examines the durability properties of Class 1 (50–75 MPa) high-performance concrete (HPC) blended with rice husk ash (RHA) as a partial replacement of CEM II B-L, 42.5 N. Six HPC mixes were prepared with RHA and used as 5%, 10%, 15%, 20%, 25%, and 30% of CEM II alone and properties are compared with control mix having only CEM II. The binders (CEM II and RHA) were investigated for particle size distribution (PSD), specific surface area (SSA), oxide compositions, mineralogical phases, morphology, and functional groups using advanced techniques of laser PSD, Brunauer–Emmett–Teller (BET), X-ray fluorescence (XRF), X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared/attenuated total reflection (FTIR/ATR), respectively, to understand their import on HPC. Durability properties, including water absorption, sorptivity, and chemical attack of the HPC samples, were investigated to realise the effect of RHA on the HPC matrix. The findings revealed that the durability properties of RHA-based HPCs exhibited an acceptable range of values consistent with relevant standards. The findings established that self-produced RHA would be beneficial as a cement replacement in HPC. As the RHA is a cost-effective agro-waste, a scalable product of RHA would be a resource for sustainable technology.

Supplementary cementitious materials (SCMs) have been widely used to enhance both the microscopic and macroscopic properties of the Portland cement (PC)–SCM composite matrix. Few studies have been undertaken to establish the gel/space ratio of meta-illite calcined clay (MCC) and rice husk ash (RHA)-based high-performance concrete (HPC) mortar. This experimental paper describes a conventional degree of hydration (non-evaporable water) and porosity routes of establishing a link amid the gel/space ratio and compressive strength of a sieved mortar from Class 1 (50–75 MPa) HPC at an early age. Using the non-evaporable water method, this paper predicted the gel/space ratio of the hardened MCC/RHA-based HPC mortars and curved fitted into Powers’ exponent equation. The results from this study revealed that MCC or RHA additions (5–30% by weight of PC) to the PC-SCM matrix led to a moderate decline in the compressive strength of the low water-binder ratio (W/B) HPC mortar. The modification aimed at void volume (superabsorbent polymers, SAP, and air) applying Bolomey’s formula and Powers’ gel/space ratio developed a suitable fitting into the Powers’ model. This experimental procedure shows feasibility to predict the MCC and RHA outcome on the compressive strength of HPC.

The work described in this paper has been performed to determine the potential use of meta-illite (K_yAl₄(Si_8-y) O₂₀(OH)₄) calcined clay (MCC) as a supplementary cementitious material (SCM) in a binary Portland cement (PC) for high-performance concrete (HPC) production. To obtain the properties of the cementitious materials, the chemical composition, mineral phases, morphology, calcination efficiency and physical properties were quantitatively analysed using the advanced techniques of X-ray fluorescence (XRF), scanning electron microscopy/energy dispersive X-ray (SEM/EDX), X-ray diffraction (XRD), Fourier transform infrared/attenuated total reflection (FTIR/ATR), thermogravimetric analysis (TGA), laser particle sizing and Brunauer–Emmett–Teller (BET) nitrogen absorption method. The MCC’s effect on the workability and mechanical properties (compressive, splitting tensile and flexural strengths) and microstructure (morphology and crystalline phases) of hardened MCC-based HPCs were determined. The XRF result shows that the oxide composition of MCC confirmed the pozzolanic material requirements with recorded high useful oxides content. At the same time, the SEM image presents particles of broad, solid masses with a wider surface area of irregular shape. The XRD results show that the MCC was majorly an illite-based clay mineral calcined at a maximum temperature of 650 °C, as revealed by the TGA. The MCC addition increases the slump flow of HPCs at 5–15% cement replacement. The MCC incorporation at 10% cement replacement best improved the porosity of HPCs at a later age resulting in increased mechanical and microstructural properties of tested samples. Therefore, it is recommended that MCC addition within 10% cement replacement be adopted for low W/B Class I HPC at no deleterious results on mechanical and microstructural properties of the concrete.

Superabsorbent polymers (SAP) addition as an internal curing (IC) agent in concrete is an approach being adopted for the mitigation of autogenous shrinkage. Micro-voids created by SAP are arguably believed to be detrimental to the mechanical properties especially the fracture tendencies of the concrete. This paper presents the report of an experimental study of SAP’s influence on the splitting tensile strength and fracture energy of low water/binder (W/B) high-performance concrete (HPC). Reference HPC mixtures (M1F, M1S, M2 and M3) designed for a 28-day minimum cube compressive strength of 70 N/mm² (MPa) were examined for the effect of SAP grain size, content and binder type on the above stated properties. Wedge splitting test was carried out on 100 mm cube specimen of HPC containing varied SAP contents (0.2, 0.3 and 0.4 by weight of binder (bwob)) and SAP sizes, cured by water immersion for 28, 56 and 90 days respectively. The results obtained was plotted as splitting force (Fsp in kN) against the crack mouth opening displacement (CMOD in mm) for computing the work of fracture (Wf), which is the area under the Fsp CMOD curve. The study concludes that the splitting tensile strength and fracture energy of the HPCs are not directly affected by SAP addition (i.e. neither grain size nor content).