It is now more popular to use basalt fibers in the engineering programs to reinforce the crack resistance of asphalt mixtures. However, research concerning the impact of the basalt fiber diameter on the macro performance of AC-13 mixtures is very limited. Therefore, in this paper, basalt fibers with three diameters, including 7, 13 and 25 μm, were selected to research the influences of fiber diameter on the crack resistance of asphalt mixtures. Different types of crack tests, such as the low temperature trabecular bending test (LTTB), the indirect tensile asphalt cracking test (IDEAL-CT), and the semi-circular bend test (SCB), were conducted to reveal the crack resistance of AC-13 mixtures. The entire cracking process was recorded through the digital image correlation (DIC) technique, and the displacement cloud pictures, strain, average crack propagation rate (V) and fracture toughness (FT) indicators were used to evaluate the crack inhibition action of the fiber diameter on the mixture. The results showed that the incorporation of basalt fiber substantially improved the crack resistance, slowed down the increase of the displacement, and delayed the fracture time. Basalt fiber with a diameter of 7 μm presented the best enhancement capability on the crack resistance of the AC-13 mixture. The flexibility index (FI) of the SCB test showed a good correlation with V and FT values of DIC test results, respectively. These findings provide theoretical advice for the popularization and engineering application of basalt fibers in asphalt pavement.

Basalt fiber has been widely used in asphalt mixture due to its excellent mechanical properties and good combination with asphalt. In order to systematically evaluate the enhancement effect of basalt fiber on the fatigue performance of the mixtures, gradations of Stone Mastic Asphalt and Superpave with different nominal maximum aggregate sizes, namely SMA-13, SUP-20 and SUP-25, were prepared, and a four-point bending beam fatigue test was adopted under the strain control mode. The fatigue damage mode was assessed based on the phenomenology theory, energy dissipation theory and change rate of dissipated energy. The results showed that basalt fiber could well increase the fatigue life of the mixtures. Basalt fiber could also increase the cumulative dissipated energy of the mixtures, and it was linearly correlated with the fatigue life in double logarithmic coordinates. In the meantime, adding basalt fiber could increase the change rate of dissipated energy of the mixtures. Furthermore, it is not appropriate to take the stiffness modulus declined to 50% of the original as the fatigue failure criterion of the mixture; this paper suggested that it is reasonable when the stiffness modulus was 15–25% that of the initial. These findings provide a theoretical basis for exploring the fatigue failure of asphalt pavements.