All-solid-state batteries (ASSBs) are a promising response to the need for safety and high energy density of large-scale energy storage systems in challenging applications such as electric vehicles and grid integration. ASSBs based on sulfide solid electrolytes (SEs) have attracted much attention because of their high ionic conductivity and wide electrochemical windows of the sulfide SEs. Here, we study the electrochemical performance of ASSBs using composite electrodes prepared via two processes (simple mixture and solution processes) and varying the ionic conductor additive (80Li₂S∙20P₂S₅ and argyrodite-type Li₆PS₅Cl). The composite electrodes consist of lithium-silicate-coated LiNi_1/3Mn_1/3Co_1/3O₂ (NMC), a sulfide SE, and carbon additives. The charge-transfer resistance at the interface of the solid electrolyte and NMC is the main parameter related to the ASSB’s status. This value decreases when the composite electrodes are prepared via a solution process. The lithium silicate coating and the use of a high-Li-ion additive conductor are also important to reduce the interfacial resistance and achieve high initial capacities (140 mAh g⁻¹).

Ammoniacal thiosulfate has been used lately as an alternative lixiviant for leaching gold from sulfides ores which are not amenable for cyanidation. However, the oxidation of the sulfide minerals generates products that inhibit the dissolution of gold and can promote the degradation of the leaching solution. The complexity of the ammoniacal thiosulfate leaching system has prevented the unification and clarification of the mechanisms of oxidation of sulfide ores used for gold extraction.