The goal of this work is to develop a sustainable value chain of carbonaceous adsorbents that can be produced from the solid fibrous digestate (SFD) of biogas plants and further applied in integrated desulfurization-upgrading (CO₂/CH₄ separation) processes of biogas to yield high-purity biomethane. For this purpose, physical and chemical activation of the SFD-derived BC was optimized to afford micro-mesoporous activated carbons (ACs) of high BET surface area (590–2300 m²g⁻¹) and enhanced pore volume (0.57–1.0 cm³g⁻¹). Gas breakthrough experiments from fixed bed columns of the obtained ACs, using real biogas mixture as feedstock, unveiled that the physical and chemical activation led to different types of ACs, which were sufficient for biogas upgrade and biogas desulfurization, respectively. Performing breakthrough experiments at three temperatures close to ambient, it was possible to define the optimum conditions for enhanced H₂S/CO₂ separation. It was also concluded that the H₂S adsorption capacity was significantly affected by the restriction to gas diffusion. Hence, the best performance was obtained at 50 °C, and the maximum observed in the H₂S adsorption capacity vs. the temperature was attributed to the counterbalance between adsorption and diffusion processes.

Polyamide microcapsules have gathered significant research interest during the past years due to their good barrier properties; however, the potential of their application is limited due to the fragility of the polymeric membrane. Fully aliphatic polyamide microcapsules (PA MCs) were herein prepared from ethylene diamine and sebacoyl chloride via interfacial polymerization, and the effect of key encapsulation parameters, i.e., monomers ratio, core solvent, stirring rate and time during the polymerization step, were examined concerning attainable process yield and microcapsule properties (shell molecular weight and thermal properties, MC size and morphology). The process yield was found to be mainly influenced by the nature of the organic solvent, which was correlated to the diffusion potential of the diamine from the aqueous phase to the organic core through the polyamide membrane. Thus, spherical microcapsules with a size between 14 and 90 μm and a yield of 33% were prepared by using toluene as core solvent. Milder stirring during the polymerization step led to an improved microcapsule morphology; yet, the substantial improvement of mechanical properties remains a challenge.