We attempted surface modification in ZnO nanoparticles (NPs) synthesized by the sol–gel process with polyvinyl pyrrolidone (PVP) applied to bulk-heterojunction polymer solar cells (PSCs) as an electron transport layer (ETL). In general, ZnO NPs have trap sites due to oxygen vacancies which capture electrons and degrade the performance of the PSCs. Devices with six different PVP:Zn ratios (0.615 g, 1.230 g, 1.846 g, 2.460 g, 3.075 g, and 3.690 g) were fabricated for surface modification, and the optimized PVP:Zn ratio (2.460 g) was found for PSCs based on P3HT/PCBM. The power conversion efficiency (PCE) of the fabricated PSCs with PVP-capped ZnO exhibited a significant increase of approximately 21% in PCE and excellent air-stability as compared with the uncapped ZnO-based PSCs.

Shortwave infrared (SWIR) sensors have attracted interest due to their usefulness in applications like military and medical equipment. SWIR sensors based on various materials are currently being studied. However, most SWIR detectors need additional optical filters and cooling systems to detect specific wavelengths. In order to overcome these limitations, we proposed a solution processed SWIR sensor that can operate at room temperature using lead chloride (PbS) QDs as a photoactive layer. Additionally, we adapted zinc oxide (ZnO) nanoparticles (NPs) as an electron transport layer (ETL) to improve the sensitivity of a PbS SWIR sensor. In this study, PbS SWIR sensors with and without a ZnO NPs layer were fabricated and their current–voltage (I–V) characteristics were measured. The on/off ratio of the PbS SWIR sensor with ZnO NPs was 2.87 times higher than that of the PbS SWIR sensor without ZnO NPs at the maximum current difference. The PbS SWIR sensor with ZnO NPs showed more stable current characteristics than that without ZnO NPs because of the ZnO NPs’ high electron mobility and proper lowest unoccupied molecular orbital (LUMO) level.

In this study, we developed a pore size/pore area-controlled optical biosensor-based anodic aluminum oxide (AAO) nanostructure. As the pore size of AAO increases, the unit cell of AAO increases, which also increases the non-pore area to which the antibody binds. The increase in the number of antibodies immobilized on the surface of the AAO enables effective detection of trace amounts of antigen, because increased antigen-antibody bonding results in a larger surface refractive index change. High sensitivity was thus achieved through amplification of the interference wave of two vertically-incident reflected waves through the localized surface plasmon resonance phenomenon. The sensitivity of the fabricated sensor was evaluated by measuring the change in wavelength with the change in the refractive index of the device surface, and sensitivity was increased with increasing pore-size and non-pore area. The sensitivity of the fabricated sensor was improved and up to 11.8 ag/mL serum amyloid A1 antigen was detected. In addition, the selectivity of the fabricated sensor was confirmed through a reaction with a heterogeneous substance, C-reactive protein antigen. By using hard anodization during fabrication of the AAO, the fabrication time of the device was reduced and the AAO chip was fabricated quickly and easily.

In bulk heterojunction polymer solar cells (BHJ-PSCs), poly(3,4-ethylenedioxythiophene) doped with poly(styrene sulfonate) (PEDOT:PSS) is the most commonly used hole selective interlayer (HSIL). However, its acidity, hygroscopic nature, and the use of indium tin oxide (ITO) etching can degrade the overall photovoltaic performance and the air-stability of BHJ-PSCs. Solvent engineering is considered as a facile approach to overcome these issues. In this work, we engineered the HSIL using ethanol (ET) treated PEDOT:PSS to simultaneously enhance the photovoltaic performance properties and air-stability of the fabricated devices. We systematically investigated the influence of ET on the microstructural, morphological, interfacial characteristics of modified HSIL and photovoltaic characteristics of BHJ-PSCs. Compared with the BHJ-PSC with pristine PEDOT:PSS, a significant enhancement of power conversion efficiency (~17%) was witnessed for the BHJ-PSC with PEDOT:PSS-ET (v/v, 1:0.5). Consequently, the BHJ-PSC with PEDOT:PSS-ET (v/v, 1:0.5) as HSIL exhibited remarkably improved air-stability.