Irreversible climate change, including atmosphere temperature extremes, is one of the most important issues of the present time. In this context, the construction industry requires solutions for increasing the energy efficiency of buildings through feedback between temperature adjustment inside buildings and better isolation of the external parts of buildings. Newly developed thermal insulation materials play an important role in this strategy. This paper presents the foamed geopolymer based on metakaolin that can be used as a modern facade material. In order to further improve its thermal insulation properties, the composition of geopolymer was modified with organic substances, i.e., perlite and cellulose fibers (30% and 50% of the volume). The thermal conductivity and insulation properties, density, mineral phases, absorbability, and compressive strength were improved for composite materials. It has been shown that the final properties of the foamed geopolymer can be controlled to a great extent by modifications, and the final properties determine its applicability.

The purpose of this study was to investigate the properties of hardened alkali-activated concrete, which is considered an eco-friendly alternative to Portland cement concrete. In this paper, the precursors for alkali-activated concrete preparations are blends of fly ash and ground-granulated blast-furnace slag in three slag proportions: 5%, 20%, and 35%, expressed as a percentage of fly ash mass. Thus, three concretes were designed and cast, denominated as AAC5, AAC20, and AAC35. Their physical and mechanical characteristics were investigated at 28 and 180 days, as well as their properties of chloride ion transport. The modified NT BUILD 492 migration test was applied to determine the chloride ions’ penetration of the alkali-activated concretes. Improvement of mechanical strength and resistance to chloride aggression was observed with ground-granulated blast-furnace slag content increase in the compositions of the tested concretes. Mercury intrusion porosimetry tests provided insight into the open pore structures of concretes. A significant decrease in the total pore volume of the concrete and a change in the nature of the pore diameter distribution due to the addition of ground granulated blast furnace slag were demonstrated.

Alkali-activated materials (AAM) are binders that are considered an eco-friendly alternative to conventional binders based on Portland cement. The utilization of industrial wastes such as fly ash (FA) and ground granulated blast furnace slag (GGBFS) instead of cement enables a reduction of the CO₂ emissions caused by clinker production. Although researchers are highly interested in the use of alkali-activated concrete (AAC) in construction, its application remains very restricted. As many standards for hydraulic concrete’s gas permeability evaluation require a specific drying temperature, we would like to emphasize the sensitivity of AAM to such preconditioning. Therefore, this paper presents the impact of different drying temperatures on gas permeability and pore structure for AAC5, AAC20, and AAC35, which contain alkali-activated (AA) binders made from blends of FA and GGBFS in slag proportions of 5%, 20%, and 35% by the mass of FA, respectively. The preconditioning of samples was performed at 20, 40, 80, and 105 °C, up to the obtainment of constant mass, and then gas permeability was evaluated, as well as porosity and pore size distribution (mercury intrusion porosity (MIP) for 20 and 105 °C). The experimental results demonstrate up to a three-percentage-point rise in the total porosity of low-slag concrete after 105 °C in comparison to 20 °C, as well as a significant increase in gas permeability, reaching up to 30-fold amplification, contingent upon the matrix composition. Notably, the alteration in pore size distribution, influenced by the preconditioning temperature, exhibits a substantial impact. The results highlight an important sensitivity of permeability to thermal preconditioning.

The main aim of this article, carried out in relation to ash–cement mortars, is to determine the effect of complex additives of polyfunctional modifiers, including, in addition to superplasticizers, air-entraining and water-retaining additives, at different values of water–cement ratios. With the use of experimental–statistical models, the complex effect on the adhesive strength of cement–ash mortars of water–cement and ash–cement ratios, as well as complex additives of polyfunctional modifiers, including air-entraining and water-retaining additives, is considered. The extreme nature of the water–cement and ash–cement ratios on the adhesive strength of ash–cement mortars are established. Their optimal values are in the ranges of 0.7–0.75 and 0.35–0.4, respectively. The addition of a naphthalene-formaldehyde superplasticizer makes it possible to increase the adhesive strength of mortars by up to 40%. A positive effect is achieved along with the addition of a superplasticizer by introducing optimal amounts of air-entraining and water-retaining additives into the mortar mixtures. Quantitative parameters of mortar compositions that positively affect adhesive strength are established. The influence on the adhesive strength of the fly ash was also investigated, as well as on the binder–sand ratio. In addition, a positive effect on the adhesive strength of modified cement–ash mortars was experimentally shown by increasing the specific surface area of fly ash by regrinding it and increasing the cement–sand ratio.

Due to the need to reduce the CO₂ emissions of mineral binders, researchers are considering the use of alkali-activated materials (AAMs) as an alternative to cementitious binders. The properties of AAMs can be more advantageous than those presented by cementitious binders, and thus they can replace Portland cement binders in some applications. Mechanical tests of AAMs are being conducted on an ongoing basis; however, durability issues related to reinforcing steel in conditions in which steel members interact with chloride ions remain unsolved. In this paper, the precursors for AAM preparations are blends of fly ash (FA) and ground granulated blast-furnace slag (GGBFS) in four slag proportions: 0%, 10%, 30% and 50% expressed as a percent of FA mass. Four alkali-activated mortars were prepared, denominated as AAM 0, AAM 10, AAM 30 and AAM 50, respectively. Their basic physical and mechanical characteristics were investigated, as were their gas transport properties. The nitrogen Cembureau method was applied to determine the permeability of the mortar. The transport properties of the chloride ions were determined using the modified NT BUILD 492 migration test. The comparison of results obtained demonstrated a positive effect of GGBFS addition in terms of an increase in bulk density, permeability, porosity and, at the same time, a reduction in chloride ion penetration. The water absorption tests also provided insight into the open pore structures of mortars. The measurements revealed a strong dependence between fluid transport through the mortars and the water absorption and initial water content of materials.