The mechanical properties of cementitious composites before and after exposure to high temperature are affected by calcium–silicate–hydrate (C–S–H) gels. To evaluate the effects of high temperature, plyvinyl alcohol (PVA) fiber content, and the cooling method on properties of cementitious composites, physical, mechanical, and microscopic tests were performed in this study. The target temperatures were 25, 100, 200, 300, 400, 600, and 800 °C. The PVA fiber contents were 0.0, 0.3, 0.6, 0.9, 1.2, and 1.5 vol%. The high-temperature resistance of PVA fiber-reinforced cementitious composite (PVA-FRCC) specimens was investigated through changes in their appearance, mass loss, compressive strength, splitting tensile strength, flexural strength, and microstructure. The results showed that PVA fibers reduced the probability of explosion spalling in the PVA-FRCC specimens exposed to high temperatures. The mass loss rate of samples exposed to temperatures below 200 °C was small and lower than 5%, whereas a significant mass loss was observed at 200 °C to 800 °C. A small rise in the cubic compressive and splitting tensile strengths of samples was found at 400 °C and 300 °C, respectively. Below 400 °C, the fibers were beneficial to the mechanical strength of the PVA-FRCC specimens. Nevertheless, when the temperature was heated above 400 °C, melted fibers created many pores and channels, which caused a decrease in the strength of the specimens. The method of cooling with water could aggravate the damage to the cementitious composites exposed to temperatures above 200 °C. High temperature could lead to the decomposition of the C–S–H gels of the PVA-FRCC samples, which makes C–S–H gels lose their bonding ability. From the perspective of the microstructure, the structure of PVA-FRCC samples exposed to 600 °C and 800 °C became loose and the number of microcracks increased, which confirmed the reduction in macro-mechanical properties.

In this study, the mechanical behaviors of nano-SiO₂ reinforced geopolymer concrete (NS-GPC) under the coupling effect of a wet–thermal and chloride salt environment were investigated through a series of basic experiments, and a simulation on the coupling effect of a wet–thermal and chloride salt environment and SEM test were also included. During the experiments for the coupling effect of the wet–thermal and chloride salt environment, an environment simulation test chamber was utilized to simulate the wet–thermal and chloride salt environment, in which the parameters of relative humidity, temperature, mass fraction of NaCl solution and action time were set as 100%, 45 °C, 5% and 60 d, respectively. The content of nano-SiO₂ (NS) particles added in geopolymer concrete (GPC) were 0, 0.5%, 1.0%, 1.5% and 2.0%. The result indicated that the mechanical properties of NS reinforced GPC decreased under the coupling effect of the wet–thermal and chloride salt environment compared to the control group in the natural environment. When the NS content was 1.5%, the cube and splitting tensile strength, elastic modulus and impact toughness of GPC under the coupling environment of wet–thermal and chloride salt were decreased by 9.7%, 9.8%, 19.2% and 44.4%, respectively, relative to that of the GPC under the natural environment. The addition of NS improved the mechanical properties of GPC under the coupling effect of the wet–thermal and chloride salt environment. Compared to the control group without NS, the maximum increment in cube compressive strength, splitting tensile strength and elastic modulus of NS–GPC under the coupling effect of the wet–thermal and chloride salt environment due to the incorporation of NS reached 25.8%, 9.6% and 17.2%, respectively. Specifically, 1.5% content of NS increased the impact toughness, impact numbers of initial crack and the ultimate failure of GPC by 122.3%, 109% and 109.5%, respectively.

A large quantity of particulate matter is generated during construction of civil engineering projects, which has a negative effect on the atmosphere and environment. In order to explore the concentration, distribution and diffusion of particulate matters generated from construction dust with different moisture contents, a wind tunnel experiment was conducted, and the effects of wind speed and moisture content on the inhibition rate, drifting distance and suppression percentage of particulate matters were investigated. The results show that the peak concentration decreases with the increase in moisture content, compared with dry dust; the peak concentrations for 1%, 2% and 3% moisture content are reduced by 37.07%, 39.53% and 65.38%, respectively. The average concentrations in the cross-section decrease with the increase in the moisture content, resulting in an increasing tendency of the particle inhibition rate. The forecast drifting distance decreases with the increase in the moisture content; when the suspension percentage is 1%, the forecast drifting distances of dry dust, 1%, 2% and 3% moisture content are 641.58, 116.08, 19.33 and 3.82 km, respectively, for a 5 m/s wind speed. Considering that an increase in wind velocity will not only decrease the inhibition rate but also increase the drifting distance, the dust suppression method by increasing the moisture content in low and medium wind velocities is applicable. When the limit value of the particle suppression rate within a distance of 50 m is larger than 70%, construction activities are prohibited at any wind velocity for dry and 1% moisture content, and at wind velocities larger than 2 m/s and 4 m/s for 2% and 3% moisture content, respectively.

This paper investigates the effects of steel fiber and PVA fiber hybrid blending on the compressive strength ($f_{\mathrm{c}\mathrm{c}}$), splitting tensile strength ($f_{\mathrm{t}\mathrm{s}}$), compression energy ($W_{1.0}$), and shrinkage properties of concrete. It also establishes a multi-factor crack resistance index evaluation model based on the Analytic Hierarchy Process (AHP) to comprehensively evaluate the crack resistance of concrete. The results show that the steel–PVA hybrid fiber (S-PVA HF) further enhances $f_{\mathrm{c}\mathrm{c}}$, $f_{\mathrm{t}\mathrm{s}}$, the compression energy, and the shrinkage suppression properties of the concrete. The crack resistance of the steel–PVA hybrid fiber concrete (S-PVA HFRC) is the best when the proportion of steel fiber is 1.0% and that of the PVA fiber is 0.2%, and it increases up to 143% compared to the baseline concrete. The established concrete crack resistance evaluation model has a certain reliability.

The application of concrete containing mineral admixtures was attempted in Northwest China in this study, where the environment has the characteristics of low humidity and large temperature variation. The harsh environment was simulated by using an environmental chamber in the laboratory and four types of concrete were prepared, including ordinary concrete and three kinds of mineral admixture concretes with different contents of fly ash and blast-furnace slag. These concretes were cured in the environmental chamber according to the real curing conditions during construction. The compression strength, fracture properties, SEM images, air-void characteristics, and X-ray diffraction features were researched at the early ages of curing before 28 d. The results showed that the addition of fly ash and slag can improve the compression strength and fracture properties of concrete in the environment of low humidity and large temperature variation. The optimal mixing of mineral admixture was 10% fly ash and 20% slag by replacing the cement in concrete, which can improve the compression strength, initial fracture toughness, unstable fracture toughness, and fracture energy by 23.9%, 25.2%, 45.3%, and 22.6%, respectively, compared to ordinary concrete. Through the analysis of the microstructure of concrete, the addition of fly ash and slag can weaken the negative effects of the harsh environment of low humidity and large temperature variation on concrete microstructure and cement hydration.

The large temperature difference condition in Northwest China threatens a myriad of concrete structures during construction, with the daily temperature varying by around 40 °C. To investigate the macro-mechanical properties and microstructural characteristics of concrete containing different amounts of mineral admixtures under such harsh conditions, this investigation used an environmental chamber to simulate a saline soil erosion environment with a large temperature difference. Four types of concrete containing different proportions of fly ash and slag were prepared and exposed in the environmental chamber with a daily temperature change of −5~40 °C to investigate their compressive strength, flexural strength, and fracture properties. Moreover, the X-ray diffraction (XRD) characteristics, microscopic morphological characteristics, pore structure characteristics, and post-erosion chloride ion distribution characteristics were also observed and recorded. Results showed that the mineral admixture could improve the early strength development of the concrete and effectively improve the fracture performance of the concrete. The average compressive strength growth rate of concrete from day 3 to day 14 was 83.25% higher than that of ordinary concrete (OC) when 15% fly ash and 15% slag were added. In addition, the fracture energy of the concrete was maximized when 15% fly ash and 20% slag were added, which was 50.67% higher than that of OC; furthermore, the internal compactness and pore structure were optimized, and the resistance to saline soil erosion was strong. This provides a basis for the practical application of compounded mineral admixture-modified concrete in an arid environment with a large temperature difference and saline soil erosion.