This study was conducted to investigate the characteristics of the AlCrCuFeNi high-entropy alloy (HEA) synthesized through mechanical alloying (MA). In addition, effects of Process Control Agent (PCA) amount and milling time were investigated using X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS). The results indicated that the synthesized AlCrCuFeNi alloy is a dual phase (FCC + BCC) HEA and the formation of the phases is strongly affected by the PCA amount. A high amount of PCA postponed the alloying process and prevented solid solution formation. Furthermore, with an increase in the PCA amount, lattice strain decreased, crystallite size increased, and the morphology of the mechanically alloyed particles changed from spherical to a plate-like shape. Additionally, investigation of thermal properties and annealing behavior at different temperatures revealed no phase transformation up to 400 °C; however, the amount of the phases changed. By increasing the temperature to 600 °C, a sigma phase (σ) and a B2-ordered solid solution formed; moreover, at 800 °C, the FCC phase decomposed into two different FCC phases.

An aluminum matrix composite with dispersed carbon nanotubes (CNTs) was produced via flake powder metallurgy using a micro-rolling process and vacuum hot pressing (VHP), followed by conventional rolling using a macro-rolling process. The microstructure and mechanical properties of the produced composites were studied. In addition, a new quantitative model was introduced to study the dislocation density based on the microstructural parameters. The results revealed that the distribution characteristics of the CNTs in the Al matrix and the Al-CNT interfaces were the two main governing parameters of dislocation density. Moreover, the dependence of dislocation density on the geometry of the grains and crystallographic texture was shown in this model. The microstructural evolution revealed that a lamellar grain structure had been achieved, with a high capacity for the storage of dislocation. A uniform distribution of CNTs with high bonding quality was also seen in the final microstructure.