Cerium oxide nanoparticles were prepared by a precipitation method using Ce(IV) sulphate as precursor dispersed in glycerol with varying synthesis parameters such as temperature or precipitating agent. The structural and morphological characteristics of the obtained nanoparticles were investigated by X-ray diffraction, transmission electron microscopy, and diffuse reflectance spectroscopy. The crystallite size of the nanoparticles varied between 13 and 17 nm. The presence of Ce³⁺ and Ce⁴⁺ was proved by XPS data in the CeO₂ samples and the conservation of the fluorite structure was evinced by X-ray diffractograms with a contraction of the lattice parameter, regardless of the size of the nanoparticle. From diffuse reflectance spectra, two band gap energy values for the direct transition were observed. Depending on the synthesis condition, the red shift of gap energy and the blue shift of Urbach energy with increasing content of Ce³⁺ were ascertained. The antibacterial tests revealed that the cerium oxide nanoparticles show good antimicrobial activity towards the common pathogens Escherichia coli and Staphylococcus aureus.

The effects of electron beam irradiation on the properties of ethylene propylene diene monomer (EPDM)/butyl rubber composites in presence of a polyfunctional monomer were investigated by means of differential scanning calorimetry (DSC), thermal analysis, scanning electron microscopy (SEM), attenuated total reflection absorption infrared spectroscopy (ATR-IR), and mechanical and surface energy measurements. The samples were exposed over a wide range of irradiation doses (20–150 kGy). The EPDM matrix was modified with butyl rubber, chlorobutyl rubber, and bromobutyl rubber. The gel content and crosslink density were found to increase with the electron beam irradiation dose. The values of the hardness and modulus increased gradually with the irradiation dose, while the tensile strength and elongation at break decreased with increasing irradiation dose. The EPDM/butyl rubber composites presented a higher thermal stability compared to the initial EPDM sample. The incorporation of butyl rubbers into the EPDM matrix led to an increase in material hydrophobicity. A similar trend was observed when the irradiation dose increased. The greatest change in the surface free energy and the contact angles occurs at an irradiation dose of 20 kGy. The Charlesby–Pinner plots prove the tendency to crosslinking as the irradiation dose increases.

Polymer nanocomposite films based on poly(vinyl pyrrolidone) incorporated with different amounts of copper oxide (CuO) nanoparticles were prepared by the solution casting technique. The PVP/CuO nanocomposites were analyzed by X-ray diffractometry (XRD), scanning electron microscopy, UV–Visible absorption spectroscopy and dielectric spectroscopy. The XRD analysis showed that the monoclinic structure of cupric oxide was maintained in the PVP host matrix. The key optical parameters, such as optical energy gap E_g, Urbach energy E_U, absorption coefficient and refractive index, were estimated based on the UV-Vis data. The optical characteristics of the nanocomposite films revealed that their transmittance and absorption were influenced by the addition of CuO nanoparticles in the PVP matrix. Incorporation of CuO nanoparticles into the PVP matrix led to a significant decrease in band gap energy and an increase in the refractive index. The dielectric and electrical behaviors of the PVP/CuO nanocomposites were analyzed over a frequency range between 10 Hz and 1 MHz. The effect of CuO loading on the dielectric parameters (dielectric constant and dielectric loss) of the metal oxide nanocomposites was also discussed.

EPDM/hemp fiber composites with fiber loading of 0–20 phr were prepared by the blending technique on a laboratory electrically heated roller mill. Test specimens were obtained by vulcanization using a laboratory hydraulic press. The elastomer crosslinking and the chemical modification of the hemp fiber surface were achieved by a radical reaction mechanism initiated by di(tert-butylperoxyisopropyl)benzene. The influence of the fiber loading on the mechanical properties, gel fraction, swelling ratio and crosslink degree was investigated. The gel fraction, crosslink density and rubber–hemp fiber interaction were evaluated based on equilibrium solvent-swelling measurements using the Flory–Rehner relation and Kraus and Lorenz–Park equations. The morphology of the EPDM/hemp fiber composites was analyzed by scanning electron microscopy. The water absorption increases as the hemp fiber loading increases.

The present study explores an environmentally friendly green approach to obtain cerium oxide nanoparticles via a biomediated route using Mellisa officinalis and Hypericum perforatum plant extracts as reducing agents. The as-prepared nanoparticles were studied for their structural and morphological characteristics using XRD diffractometry, scanning electron microscopy, Raman, fluorescence and electronic absorption spectra, and X-ray photoelectron spectroscopy (XPS). The XRD pattern has shown the centered fluorite crystal structure of cerium oxide nanoparticles with average crystallite size below 10 nm. These observations were in agreement with the STEM data. The cubic fluorite structure of the cerium oxide nanoparticles was confirmed by the vibrational mode around 462 cm⁻¹ due to the Ce-08 unit. The optical band gap was estimated from UV-Vis reflectance spectra, which was found to decrease from 3.24 eV to 2.98 eV. A higher specific area was determined for the sample using M. officinalis aqueous extract. The EDX data indicated that only cerium and oxygen are present in the green synthesized nanoparticles.

This study aimed to evaluate the effect of the synthesis parameters and the incorporation of natural polyphenolic extract within hydrogel networks on the mechanical and morphological properties of physically cross-linked xanthan gum/poly(vinyl alcohol) (XG/PVA) composite hydrogels prepared by multiple cryo-structuration steps. In this context, the toughness, compressive strength, and viscoelasticity of polyphenol-loaded XG/PVA composite hydrogels in comparison with those of the neat polymer networks were investigated by uniaxial compression tests and steady and oscillatory measurements under small deformation conditions. The swelling behavior, the contact angle values, and the morphological features revealed by SEM and AFM analyses were well correlated with the uniaxial compression and rheological results. The compressive tests revealed an enhancement of the network rigidity by increasing the number of cryogenic cycles. On the other hand, tough and flexible polyphenol-loaded composite films were obtained for a weight ratio between XG and PVA of 1:1 and 10 v/v% polyphenol. The gel behavior was confirmed for all composite hydrogels, as the elastic modulus (G′) was significantly greater than the viscous modulus (G″) for the entire frequency range.