Cerium oxide nanoparticles were prepared by a precipitation method using Ce(IV) sulphate as precursor dispersed in glycerol with varying synthesis parameters such as temperature or precipitating agent. The structural and morphological characteristics of the obtained nanoparticles were investigated by X-ray diffraction, transmission electron microscopy, and diffuse reflectance spectroscopy. The crystallite size of the nanoparticles varied between 13 and 17 nm. The presence of Ce³⁺ and Ce⁴⁺ was proved by XPS data in the CeO₂ samples and the conservation of the fluorite structure was evinced by X-ray diffractograms with a contraction of the lattice parameter, regardless of the size of the nanoparticle. From diffuse reflectance spectra, two band gap energy values for the direct transition were observed. Depending on the synthesis condition, the red shift of gap energy and the blue shift of Urbach energy with increasing content of Ce³⁺ were ascertained. The antibacterial tests revealed that the cerium oxide nanoparticles show good antimicrobial activity towards the common pathogens Escherichia coli and Staphylococcus aureus.

The present study explores an environmentally friendly green approach to obtain cerium oxide nanoparticles via a biomediated route using Mellisa officinalis and Hypericum perforatum plant extracts as reducing agents. The as-prepared nanoparticles were studied for their structural and morphological characteristics using XRD diffractometry, scanning electron microscopy, Raman, fluorescence and electronic absorption spectra, and X-ray photoelectron spectroscopy (XPS). The XRD pattern has shown the centered fluorite crystal structure of cerium oxide nanoparticles with average crystallite size below 10 nm. These observations were in agreement with the STEM data. The cubic fluorite structure of the cerium oxide nanoparticles was confirmed by the vibrational mode around 462 cm⁻¹ due to the Ce-08 unit. The optical band gap was estimated from UV-Vis reflectance spectra, which was found to decrease from 3.24 eV to 2.98 eV. A higher specific area was determined for the sample using M. officinalis aqueous extract. The EDX data indicated that only cerium and oxygen are present in the green synthesized nanoparticles.

Chitosan (CH) nanofibrous structures containing sulfadiazine (SDZ) or sulfadiazine modified chitosan (SCH) in the form of functional nanoparticles attached to nanofibers (hybrid nanostructures) were obtained by mono-axial and coaxial electrospinning. The mono-axial design consisted of a SDZ/CH mixture solution fed through a single nozzle while the coaxial design consisted of SCH and CH solutions separately supplied to the inner and outer nozzle (or in reverse order). The CH ability to form nanofibers assured the formation of a nanofiber mesh, while SDZ and SCH, both in form of suspensions in the electrospun solution, assured the formation of active nanoparticles which remained attached to the CH nanofiber mesh after the electrospinning process. The obtained nanostructures were morphologically characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The SDZ release profiles and kinetics were analyzed. The SDZ or SCH nanoparticles loosely attached at the surface of the nanofibers, provide a burst release in the first 20 min, which is important to stop the possible initial infection in a wound, while the SDZ and SCH from the nanoparticles which are better confined (or even encapsulated) into the CH nanofibers would be slowly released with the erosion/disruption of the CH nanofiber mesh.

Cerium oxide nanoparticles were obtained using aqueous extracts of Chelidonium majus and Viscum album. X-ray diffractometry analysis confirmed the crystalline structure of the synthesized cerium oxide nanoparticles calcined at 600 °C. Scanning electron microscopy, UV-Vis reflectance and Raman spectroscopy, XPS, and fluorescence studies were utilized to interpret the morphological and optical properties of these nanoparticles. The STEM images revealed the spherical shape of the nanoparticles and that they were predominantly uniform in size. The optical band gap of our cerium nanoparticles was determined to be 3.3 and 3.0 eV from reflectance measurements using the Tauc plots. The nanoparticle sizes evaluated from the Raman band at 464 cm⁻¹ due to the $F_{2g}$ mode of the cubic fluorite structure of cerium oxide are close to those determined from the XRD and STEM data. The fluorescence results showed emission bands at 425, 446, 467, and 480 nm. The electronic absorption spectra have exhibited an absorption band around 325 nm. The antioxidant potential of the cerium oxide nanoparticles was estimated by DPPH scavenging assay.

Herein we report on the synthesis and the effects of gradual loading of TiO₂ nanotube array layers with ZnO upon surface wettability. Two-step preparation was chosen, where TiO₂ nanotube layers, grown in a first instance by anodization of a Ti foil, were gradually loaded with controlled amounts of ZnO using the reactive RF magnetron sputtering. After crystallization annealing, the formerly amorphous TiO₂ nanotubes were converted to predominantly anatase crystalline phase, as detected by XRD measurements. The as-prepared nanotubes exhibited a well-aligned columnar structure, 1.6 μm long and 88 nm in diameter, and a small concentration of oxygen vacancies. Ti²⁺ and Ti³⁺ occur along with the Ti⁴⁺ state upon sputter-cleaning the layer surfaces from contaminants. The Ti²⁺ and Ti³⁺ signals diminish with gradual ZnO loading. As demonstrated by the VB-XPS data, the ZnO loading is accompanied by a slight narrowing of the band gap of the materials. A combined effect of material modification and surface roughness was taken into consideration to explain the evolution of surface super-hydrophilicity of the materials under UV irradiation. The loading process resulted in increasing surface wettability with approx. 33%, and in a drastic extension of activation decay, which clearly points out to the effect of ZnO-TiO₂ heterojunctions.

The electrical and optical properties stability of poly(3-hexylthiophene) (P3HT) thin films sensitized with nitromethane ferric chloride (FeCl₃) solution was investigated. The optical properties modifications were studied by spectrophotometry and ellipsometry. For electrical characterizations, electrical resistivity measurements were performed. In agreement with the observations of other authors, an important decrease in the electrical resistivity by six orders of magnitude was noticed. In addition, the repeatability and stability of this phenomenon were investigated over a few weeks after sensitization and during different cycles of heating and cooling, both in the dark and under illumination.