Porous TiNi alloys fabricated by self-propagating high-temperature synthesis (SHS) are biomaterials designed for medical application in substituting tissue lesions and they were clinically deployed more than 30 years ago. The SHS process, as a very fast and economically justified route of powder metallurgy, has distinctive features which impart special attributes to the resultant implant, facilitating its integration in terms of bio-mechanical/chemical compatibility. On the phenomenological level, the fact of high biocompatibility of porous SHS TiNi (PTN) material in vivo has been recognized and is not in dispute presently, but the rationale is somewhat disputable. The features of the SHS TiNi process led to a multifarious intermetallic Ti₄Ni₂(O,N,C)-based constituents in the amorphous-nanocrystalline superficial layer which entirely conceals the matrix and enhances the corrosion resistance of the unwrought alloy. In the current article, we briefly explore issues of the high biocompatibility level on which additional studies could be carried out, as well as recent progress and key fields of clinical application, yet allowing innovative solutions.

In this study, we assessed the outcomes after surgical treatment of thoracic post-excision defects in 15 patients, using TiNi knitted surgical meshes and customized artificial TiNi-based ribs. Methods: Eight patients were diagnosed with advanced non-small cell lung cancer (NSCLC) invading the chest wall, of which five patients were T₃N₀M₀, two were T₃N₁M₀, and one was T₃N₂M₀. Squamous cell carcinoma was identified in three of these patients and adenocarcinoma in five. In two cases, chest wall resection and repair were performed for metastases of kidney cancer after radical nephrectomy. Three-dimensional CT reconstruction and X-ray scans were used to plan the surgery and customize the reinforcing TiNi-based implants. All patients received TiNi-based devices and were prospectively followed for a few years. Results: So far, there have been no lethal outcomes, and all implanted devices were consistent in follow-up examinations. Immediate complications were noted in three cases (ejection of air through the pleural drains, paroxysm of atrial fibrillation, and pleuritis), which were conservatively managed. In the long term, no complications, aftereffects, or instability of the thoracic cage were observed. Conclusion: TiNi-based devices used for extensive thoracic lesion repair in this context are promising and reliable biomaterials that demonstrate good functional, clinical, and cosmetic outcomes.

The results are given investigations of the structural and physicomechanical properties in porous titanium nickelide, and these results are compared with analogous properties in cast alloys.

Intermetallic porous SHS–TiNi alloys exhibit tangled and specific stress–strain characteristics. This article aims to evaluate the findings emanating from experiments using standard and proprietary instruments. Fatigue testing under repeated complex loading was used to measure the total number of load cycles before failure of the SHS–TiNi samples occurred. Of the tested samples, seventy percent passed through 10 ⁶ cycles without failure due to the reversible martensite transformation in the TiNi phase, one of the prevailing constituents of a multiphase matrix. The fractured surfaces were analyzed using scanning electron microscopy and confocal laser scanning instruments. Microscopy studies showed that the entire surface of the sample is concealed by miscellaneous strata that result from the SHS processand effectively protect the porous alloy in a corrosive environment. Numerous non-metallic inclusions, which are also attributed to the SHS reaction, do not have a significant impact on the deformation behavior and fatigue performance. In this context, the successful in vivo functioning of porous grafts assessed in a canine rib-plasty model allows the bone substitute to be congruentially deformed in the body without rejection or degradation; it thus has a long operational life, often greater than 17 ×10 ⁶ (22 × 60 × 24 × 540) cycles. It acknowledges the potential benefits of SHS–TiNi as a superior osteoplastic material and its high resistance to corrosion fatigue.