The main focus of this work is to investigate the impact of varying milling times (2 to 18 h) on the structural and mechanical properties of the developed Ti-Nb-Mo alloy. The morphology, phase composition, microstructure, and mechanical behavior of milled and sintered Ti-25Nb-25Mo alloy samples were characterized systematically using x-ray diffraction, scanning electron microscope, optical microscope, and Vicker microhardness. It was noted that the quantity of the β-Ti phase increased as the milling time increased. After 12 h of milling, the synthesized alloys exhibited a spherical morphology and texture with homogeneous distribution. The milled alloys' structural evolution and morphological changes were found to be dependent on their milling duration. Morphological analysis revealed that the crystallite size and mean pore size decreased when the milling duration increased, reaching minimum values of 51 nm and < 1 μm, after 12 and 18 h respectively. As the milling time increased, the grain size decreased, resulting in an increase in density, microhardness, and elastic modulus. Ti-25Nb-25Mo will presents good anti-wear ability and higher resistance to plastic deformation due to enhanced mechanical characteristics (H/E, and H³/E²). Hence, the developed Ti-25Nb-25Mo alloys with reduced elastic modulus and desirable mechanical properties were found to be a promising option for biomedical applications.

Magnetron sputtering is one of the most commonly used deposition techniques, which has received considerable attention in industrial applications. In particular, owing to its compatibility with conventional fabrication processes, it can produce and fabricate high-quality dense thin films of a wide range of materials. In the present study, nitrogen (N) was combined with pure vanadium in order to form binary nitride to improve its mechanical and tribological performance. To evaluate the influence of nitrogen on the structure of the as-deposited vanadium nitride (VN) coatings, the following techniques were used: XPS, XRD, SEM, AFM and optical profilometry. The residual stresses were determined by the curvature method using Stoney’s formula. The hardness and Young’s modulus were obtained by nanoindentation measurements. The friction behavior and wear characteristics of the films were evaluated by using a ball-on-disk tribometer. The obtained results showed that the N/V ratio increased with increasing the N₂ flow rate while the deposition rate decreased. The preferred orientation was changed from (200) to (111) as the N₂ flow rate increased with the presence of V–N and V–O binding energies as confirmed by XPS analysis. The nitrogen addition resulted in a columnar morphology and a fine structure with fine surface roughness. The VN thin film containing 49.5 at.% of nitrogen showed the best performance: highest mechanical properties (hardness = 25 GPa), lowest friction coefficient (μ = 0.37) and lowest wear rate (W_s = 2.72 × 10⁻⁵ mm³N⁻¹ m⁻¹). A good correlation between the film microstructure, crystallite size, residual stress and mechanical and tribological properties was observed.

To purify water at low cost for our daily life, the effect of ceramic-based (mullite–cristobalite) and (mullite–zircon) powders doped with different amounts of magnesium oxide (MgO) (10 and 20 wt%) was studied. These compounds are made of a local raw material DD3 with addition of zirconia (ZrO₂) to create an open porosity. The powders were prepared by the traditional mixing method with the help of an automated crushing. The effect of MgO doping on structural, morphological and photocatalytic properties of the material was studied by various analytical techniques such as X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy, infrared, and UV–visible spectrometry. The results of XRD proved that there was a deformation in the crystal structure of the two types of ceramics after addition, which resulted in a shift of the spectra to the right, while SEM proved the presence of pores with a larger size as the proportion of MgO increases. The chemical composition of the basic components of the ceramic compounds as well as the additive was confirmed with EDS and IR spectra. The final results show that ceramics with added zirconia (DD3Z) and doped with 10% of MgO have a better photocatalytic efficiency than ceramics without zirconia. This important effect could be related to the higher rate of porosity, which provides a more active surface. The 10% MgO content showed a high photoactivity of 77.33% in only 15 min. The maximum hydrolysis rate obtained with Orange II was 92.95% after a period of 45 min with DD3Z/MgO powders.

Porous TiNi alloys fabricated by self-propagating high-temperature synthesis (SHS) are biomaterials designed for medical application in substituting tissue lesions and they were clinically deployed more than 30 years ago. The SHS process, as a very fast and economically justified route of powder metallurgy, has distinctive features which impart special attributes to the resultant implant, facilitating its integration in terms of bio-mechanical/chemical compatibility. On the phenomenological level, the fact of high biocompatibility of porous SHS TiNi (PTN) material in vivo has been recognized and is not in dispute presently, but the rationale is somewhat disputable. The features of the SHS TiNi process led to a multifarious intermetallic Ti₄Ni₂(O,N,C)-based constituents in the amorphous-nanocrystalline superficial layer which entirely conceals the matrix and enhances the corrosion resistance of the unwrought alloy. In the current article, we briefly explore issues of the high biocompatibility level on which additional studies could be carried out, as well as recent progress and key fields of clinical application, yet allowing innovative solutions.