Microtensile bond strength (μTBS) test was introduced in 1994. Since then, it has been utilized profoundly across many bond strength testing laboratories, making it currently one of the most standard and versatile bond strength test. Although it is a static and strength-based method, together with the morphological and spectroscopic investigations, it has been contributing immensely in the advancement of dentin adhesive systems. μTBS test has a greater discriminative capability than the traditional macro-shear bond test. During the early stage of its development, the authors predicted that this testing method would enable evaluation of the adhesive performances of resins to excavated carious or sclerotic dentin and the regional bond strengths of various portions of the cavity. In addition, they also stated the possibility of comparing the long-term stability of resin adhesion at various portions of the cavity walls on teeth extracted at various times after insertion of bonded restorations. In this review, we discussed the historical background, inception and the application of the μTBS test and proposed directions for further improvement of this testing method.

Teledentistry is an online dental care service that allows patients and dentists to meet in real time, safely, without being at the same location. During the COVID-19 pandemic, real-time videoconferencing has gained popularity in the field of teledentistry, with numerous benefits for both patients and dentists. Online consultations can minimize costs, maximize time, and provide more convenient care options for both patients and dentists. When practicing teledentistry, a dentist must establish a good doctor–patient relationship. Dentists must ensure that the telecommunication solution that they choose meets their clinical requirements and complies with privacy laws. Dentists should provide adequate information to patients about the limitations, advantages, and disadvantages that may occur during online consultation. Dentists must follow guidelines and procedures regarding informed consent, patient details, personal communications, and consultancies’ privacy and confidentiality. The patient should be aware of the limitations of teledentistry, and dentists will provide the best advice possible in the absence of a face-to-face consultation. This article discusses how teledentistry could be an effective tool for dentists and patients.

The removal or modification of smear layers that cover the dentin is critical to allow the penetration of adhesive molecules and to ensure a strong bond between resin and dentin. Aiming to establish a model for clinically-relevant dentin-bond testing, we evaluated the effects of smear layers created by abrasives having similar coarseness (180-grit SiC paper; fine-grit diamond bur) and application modes (single application; double application) on the microtensile bond strengths (µTBS) of two currently available universal adhesives (G-Premio Bond; Scotchbond Universal Adhesive) and a two-step self-etch adhesive (Clearfil Megabond 2). Sixty extracted human third molars were used for the μTBS test. Data were analyzed by three-way ANOVA and Tukey’s test (α = 0.05). Fracture modes were determined using stereomicroscopy. An additional 24 third molars were prepared for observation of the resin–dentin interface by TEM and adhesive-smear layer interaction by SEM. μTBS was significantly affected by the adhesives and their application modes (p < 0.001), implying that the double application of universal adhesives should be recommended to improve their performance. The effect of smear layers was not significant (p > 0.05), indicating that 180-grit SiC papers could be used to prepare dentin as a substitute for fine-grit diamond burs for dentin-bond testing in laboratory settings.

The dental adhesive market is constantly evolving to meet the demands of dentists and patients, but new products and upgrades should be rigorously evaluated before being used in clinical practice. This study investigated the physicomechanical properties and dentin bonding efficacy of a newly upgraded universal adhesive compared to its predecessor. Twenty-four molars were divided into four groups (n = 6/group) based on adhesive (new vs. predecessor) and application mode [self-etch (SE) vs. etch-and-rinse (ER)] for evaluating their dentin microtensile bond strength (μTBS), failure pattern, and bonding interface. Additional thirty-six molars’ crowns were perpendicularly sectioned to obtain flat mid-coronal dentin discs. The opposing dentin surfaces of each disc received contrasting treatments (new/predecessor adhesive applied in SE/ER mode), resulting in six interventions. The bonded discs (n = 6/intervention) were used to assess the adhesives’ survival probability employing a double-sided μTBS test. The other physicomechanical properties examined were adhesives’ oxygen inhibition layer (OIL), viscosity, hardness, elastic modulus, degree of conversion (DC), and in-situ DC. Both adhesive versions showed similar μTBS (P > 0.05), failure pattern (P > 0.05), and survival probability (P > 0.008). ER mode promoted resin tag formation and exhibited a slender adhesive layer for both adhesives. The newer adhesive version showed a thinner adhesive layer in general with narrower OIL (P < 0.001), less viscosity (P < 0.001), higher hardness (P < 0.05), elastic modulus (P < 0.05), DC (P < 0.001), and in-situ DC (P < 0.001). While the newly updated adhesive had superior physicomechanical properties with more fluidity, its dentin bonding efficacy and survival probability were comparable to its predecessor.