Microtensile bond strength (μTBS) test was introduced in 1994. Since then, it has been utilized profoundly across many bond strength testing laboratories, making it currently one of the most standard and versatile bond strength test. Although it is a static and strength-based method, together with the morphological and spectroscopic investigations, it has been contributing immensely in the advancement of dentin adhesive systems. μTBS test has a greater discriminative capability than the traditional macro-shear bond test. During the early stage of its development, the authors predicted that this testing method would enable evaluation of the adhesive performances of resins to excavated carious or sclerotic dentin and the regional bond strengths of various portions of the cavity. In addition, they also stated the possibility of comparing the long-term stability of resin adhesion at various portions of the cavity walls on teeth extracted at various times after insertion of bonded restorations. In this review, we discussed the historical background, inception and the application of the μTBS test and proposed directions for further improvement of this testing method.

Japan's largest platform for academic e-journals: J-STAGE is a full text database for reviewed academic papers published by Japanese societies

Glass-ionomer cement (GIC) is bioactive and independent. Bioactivity, which is a big trend in restorative dentistry. When they actively stimulate with microbiological species besides their primary function of restoring tooth structure then restorative materials should called “bioactive” materials. The purpose of this study was to determine the bond stability and the change in interfacial ultra-structure of a conventional glass-ionomer cement bonded to dentin, with and without pre-treatment using a polyalkenoic acid conditioner. The occlusal dentin surfaces of six teeth were ground flat. Glass-ionomer cement was bonded to the surfaces either with or without polyalkenoic acid conditioning. The teeth were sectioned into 1-mm² stick-shaped specimens. The specimens obtained were randomly assigned to two groups with different periods of storage in water: 1-week and 3-year. The micro-tensile bond strength (μTBS) was determined for each storage time. Additional specimens were prepared for interfacial analysis by using Scanning Electron Microscopy (SEM); they were produced with or without prior polyalkenoic acid conditioning in the same way as in the μTBS test. There was no significant difference in μTBS to conditioned dentin and non-conditioned dentin (p > 0.05). The failures appeared to be of a mixed nature, although aging caused more areas of cohesive than adhesive failure in both groups. Aging did not reduce the bond strength of the conventional glass-ionomer cement to dentin with or without the use of a polyalkenoic acid conditioner. Remineralized dentin layer were observed in both conditioned and unconditioned 3-years specimens.

The purpose of this study was to evaluate the microtensile bond strength (µTBS) and Knoop hardness number (KHN) of a novel experimental light-cured resin cement (HL). Eighteen flat dentin surfaces of human molars were polished using #600 SiC paper and bonded to CAD/CAM resin blocks with the respective resin cements and composites: HL, Panavia V5 (PV), and Clearfil AP-X (AP). All specimens were stored in distilled water at 37 °C for 24 h and 7 days. Scanning electron microscope (SEM) and energy dispersive X-ray (EDX) observations were performed to evaluate filler morphology and to detect the elements. The resin cements had a significant effect on the immediate µTBS (F = 22.59, p < 0.05) and after water storage µTBS (F = 22.83, p < 0.05). Significant differences (p < 0.05) in the KHN between the tested materials were observed, and HL indicated the highest KHN when compared with PV. HL showed a combination of the regular-shaped filler and spherical-shaped filler within the matrix. Silicon was detected in HL from the EDX evaluation. HL exhibited better bonding performance and polymerization, which may have contributed to the improvement of the adhesive strength.

Purpose: To morphologically evaluate the interface between a conventional glass-ionomer cement (GIC) and dentin one day after placement, as well as the changes at the interface after one year of aging/functioning in monkey teeth. Materials and Methods: On the buccal surfaces of seven intact teeth in each of two monkeys, shallow class V cavities were prepared, which were then filled with Fuji IX GP (GC) to provide 1-year in vivo data. A year later, two more teeth in each monkey were similarly prepared and restored for the 1-day in vivo group. The following day, the restored teeth were extracted and the restoration interfaces observed using transmission electron microscopy (TEM). In addition, restorations were similarly placed in two extracted human teeth (control, 1-day in vitro group) and observed a day after placement using TEM. Results: The 1-day in vivo and in vitro results showed that the GIC appeared to bond to dentin through a demineralized zone similar to the hybrid layer produced by resinous adhesives. However, the interface between GIC and dentin after 1 year in vivo appeared to change over time: many needle-like crystals were detected within the remineralized layer and along the collagen fibrils. Slow diffusion of ions resulted in pores, which filled with mineral crystals and made the pores smaller. Conclusion: The interface between GIC and dentin morphologically changes over time, and recrystallization or remineralization at the interface may occur (1 year in vivo).