Offering mild, non-invasive and deep cancer therapy modality, radio frequency (RF) radiation-induced hyperthermia lacks for efficient biodegradable RF sensitizers to selectively target cancer cells and thus avoid side effects. Here, we assess crystalline silicon (Si) based nanomaterials as sensitizers for the RF-induced therapy. Using nanoparticles produced by mechanical grinding of porous silicon and ultraclean laser-ablative synthesis, we report efficient RF-induced heating of aqueous suspensions of the nanoparticles to temperatures above 45-50 °C under relatively low nanoparticle concentrations (<1 mg/mL) and RF radiation intensities (1-5 W/cm(2)). For both types of nanoparticles the heating rate was linearly dependent on nanoparticle concentration, while laser-ablated nanoparticles demonstrated a remarkably higher heating rate than porous silicon-based ones for the whole range of the used concentrations from 0.01 to 0.4 mg/mL. The observed effect is explained by the Joule heating due to the generation of electrical currents at the nanoparticle/water interface. Profiting from the nanoparticle-based hyperthermia, we demonstrate an efficient treatment of Lewis lung carcinoma in vivo. Combined with the possibility of involvement of parallel imaging and treatment channels based on unique optical properties of Si-based nanomaterials, the proposed method promises a new landmark in the development of new modalities for mild cancer therapy.

Aqueous suspensions of porous silicon nanoparticles (NPs) with average size ∼100 nm and concentration ∼1 g/L undergo significant heating as compared with pure water under therapeutic ultrasonic (US) irradiation with frequencies of 1–2.5 MHz and intensities of 1–20 W/cm². This effect is explained by taking into account the efficient absorption of US energy by NPs. The observed US-induced heating of biodegradable NPs is promising for applications in ultrasonic hyperthermia of tumors.

Silicon nanoparticles (SiNPs) prepared by mechanical grinding of luminescent porous silicon were coated with a biopolymer (dextran) and investigated as a potential theranostic agent for bioimaging and sonodynamic therapy. Transmission electron microscopy, photoluminescence and Raman scattering measurements of dextran-coated SiNPs gave evidence of their enhanced stability in water. In vitro experiments confirmed the lower cytotoxicity of the dextran-coated NPs in comparison with uncoated ones, especially for high concentrations of about 2 mg ml ⁻¹ . Efficient uptake of the NPs by cancer cells was found using bioimaging in the optical transmittance and photoluminescence modes. Treatment of the cells with uptaken SiNPs by therapeutic ultrasound for 5–20 min resulted in a strong decrease in the number of living cells, while the total number of cells remained nearly unchanged. The obtained data indicate a ‘mild’ effect of the combined action of ultrasonic irradiation and SiNPs on cancer cells. The observed results reveal new opportunities for controlling the photoluminescent and sonosensitizing properties of silicon-based NPs for applications in the diagnostics and mild therapy of cancer.

A significant decrease of the cavitation threshold in aqueous suspensions of porous silicon nanoparticles (PSi NPs) with sizes about 100 nm as compared with pure water was observed for ultrasound irradiation (USI) with therapeutic frequency (0.88 MHz) and intensities (about 1 W/cm²). This effect is explained by porous morphology of PSi NPs, which promotes the nucleation of cavitation bubbles. In vitro experiments revealed a suppression of the proliferation of cancer cells with the introduced PSi NPs after exposure to USI related to the enhanced cavitation processes, which led to the cell destruction. The obtained results demonstrate that PSi NPs are prospective for applications as sonosensitizers in mild cancer therapy.