The nucleation and grain growth that occur during solidification have been extensively examined, but insight into the influence of an external field on the formation of heterogeneous crystal nuclei above the liquidus remains unclear in the peritectic refinement mechanism. In this work, we studied the effect of cooling rate above the liquidus on the formation of primary Al₃Zr and grain refinement in Al-0.2%Zr alloys with inter-cooling annular electromagnetic stirring (IC-AEMS). The results show that the size and distribution of primary Al₃Zr are greatly improved, and the morphology transformed from large plate/blocky shapes without IC-AEMS to small blocks with IC-AEMS. Meanwhile, above the liquidus, the addition of an Al-Zr master alloy to pure Al alone did little to enhance the refinement, but after IC-AEMS, the grains were refined dramatically. The refinement result seems to be explained by two hypotheses of pre-nucleation and explosive nucleation.

The internal coupled electromagnetic melt treatment (ICEMT) method is firstly proposed to produce high-quality and large-sized aluminum alloy billets. A three-dimensional model was established to describe the ICEMT process of direct chill casting (DC casting). The effect of ICEMT on the fluid flow patterns and temperature field in the DC casting of ϕ880 mm AA2219 billets is numerically analyzed. Moreover, the mechanisms of the ICEMT process on grain refinement and macrosegregation were discussed. The calculated results indicate that the electromagnetic field appears to be coupled circinate at the cross section of the melt, the fluid flow becomes unstable accompanied by the bias flow, and the temperature profiles are significantly more uniform. An experimental verification was conducted and the results prove that compared with traditional direct chill casting, the microstructures of the AA2219 large-scale billet under the ICEMT process are uniform and fine.