A full understanding of the impact of charge trapping on the memory window (MW) of HfO₂-based ferroelectric field effect transistors (FeFETs) will permit the design of program and erase protocols, which will guide the application of these devices and maximize their useful life. The effects of charge trapping have been studied by changing the parameters of the applied program and erase pulses in a test sequence. With increasing the pulse amplitude and pulse width, the MW increases first and then decreases, a result attributed to the competition between charge trapping (CT) and ferroelectric switching (FS). This interaction between CT and FS is analyzed in detail using a single-pulse technique. In addition, the experimental data show that the conductance modulation characteristics are affected by the CT in the analog synaptic behavior of the FeFET. Finally, a theoretical investigation is performed in Sentaurus TCAD, providing a plausible explanation of the CT effect on the memory characteristics of the FeFET. This work is helpful to the study of the endurance fatigue process caused by the CT effect and to optimizing the analog synaptic behavior of the FeFET.

The effect of high- and low-temperature conditions on the performance of IGZO TFT and logic circuits were investigated in this work. In the temperature range of 250−350 K, the performance of the IGZO TFT did not show significant changes and exhibited a certain degree of high- and low-temperature resistance. When the temperature was below 250 K, as the temperature decreased, the threshold voltage (V_TH) of the IGZO TFT significantly increased, the field effect mobility (μ_FE) and the on state current (I_ON) significantly decreased. This is attributed to the lower excitation degree of charge carriers at extremely low temperatures, resulting in fewer charge carriers transitioning to the conduction or valence bands, and the formation of defects also limits carrier migration. When the temperature exceeded 350 K, as the temperature increased, more electrons could escape from the bandgap trap state and become free charge carriers, and the IGZO layer was thermally excited to produce more oxygen vacancies, resulting in higher μ_FE and lower V_TH. In addition, the drain current noise spectral density of IGZO TFT conformed to the 1/ƒ noise characteristic, and the degradation mechanism of IGZO TFT over a wide temperature range was confirmed based on the changes in noise spectral density at different temperatures. In addition, an inverter logic unit circuit was designed based on IGZO TFT, and the performance changes over a wide temperature range were analyzed. This lays the foundation for IGZO TFT to be applied in integrated circuits with harsh environments.