Size effects, influencing a material's strength, elongation, fatigue limit, and longevity, depend on the operative and dominant deformation and failure mechanisms. This study explores the size effects in additive manufactured (AM) GRCop-42 (Cu-4at%Cr-2at%Nb) thin wall structures fabricated via laser-powder bed fusion (L-PBF) and their impact on fatigue life. The influence of internal defects and surface topography on the fatigue life of specimens in both as-built and hot isostatic pressed (HIP) conditions across different thicknesses is investigated. Where micro-computed tomography (μCT) was used to quantify the internal porosity of as-built, pristine HIP'd, and fatigued HIP'd specimens, and laser microscopy was employed to quantify the surface topography of specimens prior to fatigue. Additionally, quasi-static tests were used to establish baseline mechanical properties (i.e. yield strength (YS), ultimate tensile strength (UTS), and elongation) to frame fatigue testing conditions. Results indicate a significant enhancement in fatigue life for HIP'd specimens for both thicknesses, with internal defects depicting a greater impact than surface topography. Furthermore, fractographic analysis suggests that thicker specimens exhibit higher resistance to crack propagation during fatigue testing in the absence of substantial porosity. Thus, the size effects observed on the fatigue life of L-PBF GRCop-42 appears to be dominated by internal defects.

Laser Powder Directed Energy Deposition (LP-DED) can produce thin-wall features on the order of 1 mm. These features are essential for large structures operating in extreme environments such as regeneratively cooled nozzles and heat exchangers, which often make use of refractory metals. In this work, the mechanical behavior of LP-DED C103 was investigated via quasi-static tensile testing and low cycle fatigue (LCF) testing. The effects of vacuum stress relief (SR) and hot isostatic pressing (HIP) heat treatments were investigated for specimens in the vertical and horizontal build orientations during tensile testing. The AB and SR properties were lower than literature values for wrought and laser powder bed fusion (L-PBF) bulk components but higher than electron beam powder bed fusion (EB-PBF). The application of a HIP cycle improved strength by 7% and ductility by 27% past the initial as-built condition. Fracture images reveal that interlayer stress concentration sites are responsible for fracture in specimens in the vertical orientation. Meanwhile, fracture in the horizontal specimens mainly propagates at a slanted angle typical of plane stress conditions. The LCF results show cycles to failure ranging from 100 cycles to 8000 cycles for max strain levels of 2% and 0.5%, respectively. Fractography on the fatigue specimens reveals an increasing propagation zone as max strain levels are increased. The impact of these findings and future work are discussed in detail.