The research subject was the analysis of the microstructure, barrier properties, and mechanical resistance of the psyllium husk (PH)-modified thermoplastic starch films. The tensile tests under various static loading conditions were not performed by researchers for this type of material before and are essential for a more precise assessment of the material’s behavior under the conditions of its subsequent use. The film samples were manufactured by the casting method. PH addition improved starch gelatinization and caused a decrease in failure strain by 86% and an increase in failure stress by 48% compared to pure films. Fourier transform infrared spectroscopy results showed the formation of additional hydrogen bonds between polysaccharides in starch and PH. An increase in the number of hydrophilic groups in the modified films resulted in a faster contact angle decrease (27.4% compared to 12.8% for pure ones within the first 5 s); however, it increased the energy of water binding and surface complexity. The modified films showed the opacity at 600 nm, 43% higher than in the pure starch film, and lower transmittance, suggesting effectively improving barrier properties to UV light, a potent lipid-oxidizing agent in food systems.

The study compares the microstructure of three commercial dental cobalt matrix alloys with related chemical composition declared by the manufacturer. Casts were produced with lost wax method, then melted and casted with centrifugal induction casting machine. The Co-Cr-Mo alloys were casted...

Hole quality in composite materials is gaining interest in aerospace, automotive, and marine industries, especially for structural applications. This paper aims to investigate the quality of holes performed without a backup plate, in thin plates of glass fiber-reinforced polymer (GFRP). The samples were manufactured by two different technologies: vacuum bagging and an innovative method named vacuum mold pressing. Three experiments were designed choosing the control factors that affect the maximum cutting force, delamination factor, and surface roughness of drilled holes in composite materials based on twill fabric layers. Quality analysis of the hole features was performed by microscopy investigations. The effects of the main factors on the targets are investigated using the statistical design of experiments, considering control factors, such as support opening width, weight fraction (wf), feed per tooth, and hole area. The results showed that the feed per tooth and hole area had a more significant influence on the delamination factors and surface roughness (Sa). The best quality of the holes drilled in twill-based GFRP was achieved for a lower feed rate of 0.04 mm/tooth and used a support opening width of 55 mm.